DuPont Performance Polymers Hytrel® HTR8136BK TPC-ET (Unverified Data**)

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer	DuPont Performance Polymers
Trade Name	Hytrel®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Hytrel® HTR8136BK TPC-ET (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Hytrel® HTR8136BK is designed for blow molding or processing by techniques requiring high melt viscosity. It has nominal durometer hardness of 49D, is pigmented black with fine particle size carbon black, and contains a general purpose stabilizer.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Specific Gravity	1.16 g/cc	1.16 g/cc	ASTM D792
Density	1.16 g/cc	0.0419 lb/in³	ISO 1183
Water Absorption	0.20 % @Temperature 23.0 °C	0.20 % @Temperature 73.4 °F	Equilibrium 50%RH; ISO 62
	0.70 % @Temperature 23.0 °C	0.70 % @Temperature 73.4 °F	Immersion 24h; ASTM D570
	0.70 % @Temperature 23.0 °C	0.70 % @Temperature 73.4 °F	Immersion 24h; ISO 62
	0.70 % @Temperature 23.0 °C	0.70 % @Temperature 73.4 °F	Saturation, immersed; ISO 62
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 230 °C	2.5 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
	2.5 g/10 min @Load 2.16 kg, Temperature 230 °C	2.5 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	<= 49	<= 49	ISO 868
	<= 50	<= 50	ASTM D2240
Tensile Strength at Break	30.7 MPa @Temperature 23.0 °C	4450 psi @Temperature 73.4 °F	ASTM D638
	35.0 MPa @Temperature 23.0 °C	5080 psi @Temperature 73.4 °F	ISO 527 (1BA bar)
Tensile Stress	5.00 MPa @Strain 5.00 %, Temperature 23.0 °C	725 psi @Strain 5.00 %, Temperature 73.4 °F	ASTM D638
	6.90 MPa @Strain 10.0 %, Temperature 23.0 °C	1000 psi @Strain 10.0 %, Temperature 73.4 °F	ASTM D638
	7.90 MPa @Strain 10.0 %, Temperature 23.0 °C	1150 psi @Strain 10.0 %, Temperature 73.4 °F	ISO 527 (1BA bar)
	8.20 MPa @Strain 15.0 %, Temperature 23.0 °C	1190 psi @Strain 15.0 %, Temperature 73.4 °F	ASTM D638
Elongation at Break	>= 300 % @Temperature 23.0 °C	>= 300 % @Temperature 73.4 °F	ISO 527 (1BA bar)
	420 % @Temperature 23.0 °C	420 % @Temperature 73.4 °F	ISO 527 (1BA bar)
	550 % @Temperature 23.0 °C	550 % @Temperature 73.4 °F	ASTM D638
Flexural Modulus	0.0530 GPa @Temperature 125 °C	7.69 ksi @Temperature 257 °F	ASTM D790
	0.112 GPa @Temperature 23.0 °C	16.2 ksi @Temperature 73.4 °F	ASTM D790
	0.115 GPa @Temperature 23.0 °C	16.7 ksi @Temperature 73.4 °F	ISO 178
	0.255 GPa @Temperature -40.0 °C	37.0 ksi @Temperature -40.0 °F	ASTM D790
Izod Impact, Notched	NB @Temperature -40.0 °C	NB @Temperature -40.0 °F	ASTM D256
Izod Impact, Notched (ISO)	NB @Temperature -40.0 °C	NB @Temperature -40.0 °F	ISO 180/1A
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 180/1A
Charpy Impact, Notched	12.2 J/cm² @Temperature -40.0 °C	58.1 ft-lb/in² @Temperature -40.0 °F	ISO 179/1eA
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	500 µm/m-°C @Temperature -40.0 - 23.0 °C	278 µin/in-°F @Temperature -40.0 - 73.4 °F	ASTM E 831
	500 µm/m-°C @Temperature 23.0 - 55.0 °C	278 µin/in-°F @Temperature 73.4 - 131 °F	ASTM E 831
	500 µm/m-°C @Temperature 55.0 - 120 °C	278 µin/in-°F @Temperature 131 - 248 °F	ASTM E 831
	500 µm/m-°C @Temperature -40.0 - 23.0 °C	278 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 23.0 - 55.0 °C	278 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 55.0 - 120 °C	278 µin/in-°F @Temperature 131 - 248 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	130 µm/m-°C @Temperature 55.0 - 120 °C	72.2 µin/in-°F @Temperature 131 - 248 °F	ASTM E 831
	130 µm/m-°C @Temperature 55.0 - 120 °C	72.2 µin/in-°F @Temperature 131 - 248 °F	ISO 11359-1/-2
	159 µm/m-°C @Temperature -40.0 - 23.0 °C	88.3 µin/in-°F @Temperature -40.0 - 73.4 °F	ASTM E 831
	159 µm/m-°C @Temperature -40.0 - 23.0 °C	88.3 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	166 µm/m-°C @Temperature 23.0 - 55.0 °C	92.2 µin/in-°F @Temperature 73.4 - 131 °F	ASTM E 831
	166 µm/m-°C @Temperature 23.0 - 55.0 °C	92.2 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
Melting Point	196 °C	385 °F	ASTM D3418
	197 °C	387 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	40.0 °C	104 °F	ISO 75-1/-2
Brittleness Temperature	-100 °C	-148 °F	ISO 974

Processing Properties	Metric	English	Comments
Melt Temperature	230 °C	446 °F	Optimum; Injection Molding
Mold Temperature	45.0 °C	113 °F	optimum; Injection Molding
	40.0 - 50.0 °C	104 - 122 °F	Injection Molding
Drying Temperature	110 °C	230 °F	Blow Molding
	110 °C	230 °F	Injection Molding
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour	Blow Molding
	3.00 - 4.00 hour	3.00 - 4.00 hour	Injection Molding
Moisture Content	<= 0.020 %	<= 0.020 %	Blow Molding
	<= 0.020 %	<= 0.020 %	Injection Molding

Descriptive Properties	Value	Comments
Additive	Antioxidant
Appearance	Black Color
Features	Abrasion Resistance
	Fatigue Resistance
	Flexibility, Low Temperature
	Grease Resistant
	Melt Strength, Good
	Viscosity, High
Forms	Pellets
Generic	TPC-ET
Material Status	Current
Part Marking Code	>TPC-ET<	ISO 11469
Processing Method	Blow Molding
Product Category	Blow Moldable Resins
	Extrusion Resins
Resin Identification	TPC-ET	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Automotive Applications