DuPont Performance Polymers Crastin® S600F20UV WT660 Polybutylene Terephthalate (PBT)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® S600F20UV WT660 Polybutylene Terephthalate (PBT).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced UV Stabilized Polybutylene Terephthalate Crastin S600F20 NC010 is an unreinforced lubricated medium viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 0.40 %

@Thickness 2.00 mm
 0.40 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 88500 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 88500 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
98730 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 98730 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
109800 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 109800 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
239900 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 239900 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
303800 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 303800 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
384600 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 384600 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Viscosity Test 130 cm³/g
130 cm³/g
ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.017 cm/cm
0.017 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Melt Flow 19.1 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 19.1 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 2.81 MPa

@Strain 1.14 %,
Temperature 150 °C
 408 psi

@Strain 1.14 %,
Temperature 302 °F
 ISO 11403-1 -2
2.88 MPa

@Strain 0.190 %,
Temperature 40.0 °C
 418 psi

@Strain 0.190 %,
Temperature 104 °F
 ISO 11403-1 -2
4.32 MPa

@Strain 1.04 %,
Temperature 90.0 °C
 627 psi

@Strain 1.04 %,
Temperature 194 °F
 ISO 11403-1 -2
6.84 MPa

@Strain 4.36 %,
Temperature 150 °C
 992 psi

@Strain 4.36 %,
Temperature 302 °F
 ISO 11403-1 -2
9.06 MPa

@Strain 7.90 %,
Temperature 150 °C
 1310 psi

@Strain 7.90 %,
Temperature 302 °F
 ISO 11403-1 -2
9.31 MPa

@Strain 0.350 %,
Temperature 23.0 °C
 1350 psi

@Strain 0.350 %,
Temperature 73.4 °F
 ISO 11403-1 -2
11.7 MPa

@Strain 3.92 %,
Temperature 90.0 °C
 1700 psi

@Strain 3.92 %,
Temperature 194 °F
 ISO 11403-1 -2
16.07 MPa

@Strain 6.99 %,
Temperature 90.0 °C
 2331 psi

@Strain 6.99 %,
Temperature 194 °F
 ISO 11403-1 -2
17.7 MPa

@Strain 0.630 %,
Temperature 0.000 °C
 2570 psi

@Strain 0.630 %,
Temperature 32.0 °F
 ISO 11403-1 -2
18.6 MPa

@Strain 10.5 %,
Temperature 90.0 °C
 2700 psi

@Strain 10.5 %,
Temperature 194 °F
 ISO 11403-1 -2
21.96 MPa

@Strain 2.10 %,
Temperature 40.0 °C
 3185 psi

@Strain 2.10 %,
Temperature 104 °F
 ISO 11403-1 -2
25.21 MPa

@Strain 0.790 %,
Temperature -40.0 °C
 3656 psi

@Strain 0.790 %,
Temperature -40.0 °F
 ISO 11403-1 -2
25.36 MPa

@Strain 0.860 %,
Temperature -20.0 °C
 3678 psi

@Strain 0.860 %,
Temperature -4.00 °F
 ISO 11403-1 -2
30.59 MPa

@Strain 5.18 %,
Temperature 40.0 °C
 4437 psi

@Strain 5.18 %,
Temperature 104 °F
 ISO 11403-1 -2
34.8 MPa

@Strain 8.60 %,
Temperature 40.0 °C
 5050 psi

@Strain 8.60 %,
Temperature 104 °F
 ISO 11403-1 -2
42.45 MPa

@Strain 1.89 %,
Temperature 23.0 °C
 6157 psi

@Strain 1.89 %,
Temperature 73.4 °F
 ISO 11403-1 -2
46.64 MPa

@Strain 1.82 %,
Temperature 0.000 °C
 6765 psi

@Strain 1.82 %,
Temperature 32.0 °F
 ISO 11403-1 -2
53.41 MPa

@Strain 1.85 %,
Temperature -40.0 °C
 7746 psi

@Strain 1.85 %,
Temperature -40.0 °F
 ISO 11403-1 -2
57.12 MPa

@Strain 2.19 %,
Temperature -20.0 °C
 8285 psi

@Strain 2.19 %,
Temperature -4.00 °F
 ISO 11403-1 -2
66.69 MPa

@Strain 3.74 %,
Temperature 0.000 °C
 9673 psi

@Strain 3.74 %,
Temperature 32.0 °F
 ISO 11403-1 -2
73.3 MPa

@Strain 2.85 %,
Temperature -40.0 °C
 10600 psi

@Strain 2.85 %,
Temperature -40.0 °F
 ISO 11403-1 -2
78.69 MPa

@Strain 4.18 %,
Temperature -20.0 °C
 11410 psi

@Strain 4.18 %,
Temperature -4.00 °F
 ISO 11403-1 -2
88.18 MPa

@Strain 4.02 %,
Temperature -40.0 °C
 12790 psi

@Strain 4.02 %,
Temperature -40.0 °F
 ISO 11403-1 -2
5.00 MPa

@Strain 0.200 %,
Time 36000 sec
 725 psi

@Strain 0.200 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
5.00 MPa

@Strain 0.220 %,
Time 360000 sec
 725 psi

@Strain 0.220 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
5.00 MPa

@Strain 0.260 %,
Time 3.60e+6 sec
 725 psi

@Strain 0.260 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
5.00 MPa

@Strain 0.190 %,
Time 3600 sec
 725 psi

@Strain 0.190 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
5.00 MPa

@Strain 0.397 %,
Time 3.60e+7 sec
 725 psi

@Strain 0.397 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
20.0 MPa

@Strain 2.61 %,
Time 3.60e+7 sec
 2900 psi

@Strain 2.61 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
30.0 MPa

@Strain 4.17 %,
Time 3.60e+6 sec
 4350 psi

@Strain 4.17 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
Tensile Strength, Yield 58.0 MPa
8410 psi
ISO 527-1/-2
Elongation at Break 30 %
30 %
Nominal; ISO 527-1/-2
Elongation at Yield 7.0 %
7.0 %
ISO 527-1/-2
Tensile Modulus 2.60 GPa
377 ksi
ISO 527-1/-2
0.2273 GPa

@Temperature 135 °C
 32.97 ksi

@Temperature 275 °F
 Dynamic; ISO 11403-1 -2
0.242 GPa

@Temperature 120 °C
 35.1 ksi

@Temperature 248 °F
 ISO 11403-1 -2
0.4473 GPa

@Temperature 75.0 °C
 64.88 ksi

@Temperature 167 °F
 Dynamic; ISO 11403-1 -2
1.259 GPa

@Temperature 40.0 °C
 182.6 ksi

@Temperature 104 °F
 ISO 11403-1 -2
1.655 GPa

@Temperature 45.0 °C
 240.0 ksi

@Temperature 113 °F
 Dynamic; ISO 11403-1 -2
2.621 GPa

@Temperature 5.00 °C
 380.1 ksi

@Temperature 41.0 °F
 Dynamic; ISO 11403-1 -2
2.783 GPa

@Temperature -20.0 °C
 403.6 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
3.004 GPa

@Temperature -45.0 °C
 435.7 ksi

@Temperature -49.0 °F
 Dynamic; ISO 11403-1 -2
3.29 GPa

@Temperature -60.0 °C
 477 ksi

@Temperature -76.0 °F
 Dynamic; ISO 11403-1 -2
3.291 GPa

@Temperature -40.0 °C
 477.3 ksi

@Temperature -40.0 °F
 ISO 11403-1 -2
Flexural Strength 85.0 MPa
12300 psi
ISO 178
Flexural Modulus 2.20 GPa
319 ksi
ISO 178
Secant Modulus 0.515 GPa

@Strain 6.27 %,
Temperature 40.0 °C
 74.7 ksi

@Strain 6.27 %,
Temperature 104 °F
 ISO 11403-1 -2
1.05 GPa

@Strain 2.10 %,
Temperature 40.0 °C
 152 ksi

@Strain 2.10 %,
Temperature 104 °F
 ISO 11403-1 -2
1.52 GPa

@Strain 0.190 %,
Temperature 40.0 °C
 220 ksi

@Strain 0.190 %,
Temperature 104 °F
 ISO 11403-1 -2
1.90 GPa

@Strain 4.96 %,
Temperature -40.0 °C
 276 ksi

@Strain 4.96 %,
Temperature -40.0 °F
 ISO 11403-1 -2
2.25 GPa

@Strain 1.89 %,
Temperature 23.0 °C
 326 ksi

@Strain 1.89 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.45 GPa

@Strain 3.22 %,
Temperature -40.0 °C
 356 ksi

@Strain 3.22 %,
Temperature -40.0 °F
 ISO 11403-1 -2