Dow DOWLEX™ 2036A Linear Low Density Polyethylene, Cast Film Grade

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Dow Chemical
Trade Name DOWLEX™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow DOWLEX™ 2036A Linear Low Density Polyethylene, Cast Film Grade.pdf
  Online Service   lookpolymers   27660005
Material Notes:
DOWLEX® 2036A Polyethylene resin is a cast film polymer having improved thermal stability for high stiffness film applications. It complies with U.S. FDA regulation 21 CFR 177.1520 c 3.2a for food packaging applications. The regulation should be consulted for complete details.Film properties below based on a film thickness of 25 µm. Data provided by Dow Chemical.
Physical Properties Metric English Comments
Density 0.935 g/cc
0.0338 lb/in³
Thickness 25.0 microns
0.984 mil
Melt Flow 2.5 g/10 min

@Load 2.16 kg
2.5 g/10 min

@Load 4.76 lb
Melt flow ratio I10/I2 is 7.1.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 15.2 MPa
2200 psi
Molded property
Film Tensile Strength at Yield, MD 17.9 MPa
2600 psi
Film Tensile Strength at Yield, TD 17.9 MPa
2600 psi
Tensile Strength, Yield 20.0 MPa
2900 psi
Molded property
Film Elongation at Break, MD 480 %
480 %
Film Elongation at Break, TD 740 %
740 %
Elongation at Break 600 %
600 %
Molded value
Elmendorf Tear Strength MD 25 g
25 g
Elmendorf Tear Strength TD 700 g
700 g
Elmendorf Tear Strength, MD 1.00 g/micron
25.4 g/mil
Elmendorf Tear Strength, TD 28.0 g/micron
711 g/mil
Dart Drop 2.00 g/micron
50.8 g/mil
Film Tensile Strength at Break, MD 56.5 MPa
8190 psi
Film Tensile Strength at Break, TD 34.5 MPa
5000 psi
Thermal Properties Metric English Comments
Vicat Softening Point 119 °C
246 °F
Optical Properties Metric English Comments
Haze 3.2 %
3.2 %
Gloss 88 %
88 %
Processing Properties Metric English Comments
Processing Temperature 274 °C
525 °F
Film extrusion temperature