SABIC Innovative Plastics Cycoloy® CY5220 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CY5220 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Non-chlorinated & non-brominated FR PC/ABS featuring good flow and impact properties. Designed for various thin wall applicationsThis data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D 792
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0050 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 18 g/10 min

@Load 2.16 kg,
Temperature 260 °C
18 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 100 %
100 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.90 GPa
421 ksi
50 mm/min; ASTM D 638
Flexural Yield Strength 100 MPa
14500 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.80 GPa
406 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 5.50 J/cm

@Temperature 23.0 °C
10.3 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C

@Thickness 3.20 mm
185 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 95.0 °C
203 °F
Rate B/50; ISO 306
Flammability, UL94 V-0

@Thickness 1.19 mm
V-0

@Thickness 0.0469 in
UL 94