Covestro Bayblend® KL 1-1430 Polycarbonate/ABS Blend
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Covestro |
| Trade Name | Bayblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Bayblend® KL 1-1430 Polycarbonate/ABS Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard grade for cars.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | |
| Water Absorption | 0.70 % | 0.70 % | Saturation in water |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Equilibrium at 50% RH |
| Water Absorption at Saturation | 0.70 % | 0.70 % | |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 260 °C |
12 g/10 min @Load 11.0 lb, Temperature 500 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal |
| Elongation at Yield | 4.0 % | 4.0 % | |
| Tensile Modulus | 2.20 GPa | 319 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 82.5 µm/m-°C @Temperature 20.0 °C |
45.8 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 85.0 µm/m-°C @Temperature 20.0 °C |
47.2 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Vicat Softening Point | 114 °C | 237 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | 22 % | 22 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.0 @Frequency 100 Hz |
2.0 @Frequency 100 Hz |
|
| 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | |
| Dissipation Factor | 0.0040 @Frequency 100 Hz |
0.0040 @Frequency 100 Hz |
|
| 0.0070 @Frequency 1e+6 Hz |
0.0070 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 300 V | 300 V |