BNZ Materials Bazelite 2600 LI Insulating Castable

Category	Ceramic , Oxide , Aluminum Oxide
Manufacturer	BNZ Materials, Inc.
Trade Name	Bazelite
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BNZ Materials Bazelite 2600 LI Insulating Castable.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Blaz 2600 LI is s low iron, high purity castable for service to 2600°F (1427°C) in controlled atmosphere applications. Recommended for casting monolithic shapes and furnace liningsInformation provided by BNZ Materials Inc.

Physical Properties	Metric	English	Comments
Density	1.15 g/cc	0.0417 lb/in³	Fired at 5 hrs at 816°C

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.000690 GPa @Temperature 1260 °C	0.100 ksi @Temperature 2300 °F	ASTM C268
	0.000760 GPa @Temperature 815 °C	0.110 ksi @Temperature 1500 °F	ASTM C268
	0.000830 GPa @Temperature 1095 °C	0.120 ksi @Temperature 2003 °F	ASTM C268
	0.00110 GPa @Temperature 540 °C	0.160 ksi @Temperature 1000 °F	Fired; ASTM C268
	0.00165 GPa @Temperature 104 °C	0.239 ksi @Temperature 219 °F	Dried; ASTM C268
	0.00207 GPa @Temperature 1371 °C	0.300 ksi @Temperature 2500 °F	ASTM C268
Compressive Strength	4.83 MPa @Temperature 815 °C	700 psi @Temperature 1500 °F	Cold Crush Strength
	4.83 MPa @Temperature 1095 °C	700 psi @Temperature 2003 °F	Cold Crush Strength
	4.83 MPa @Temperature 1260 °C	700 psi @Temperature 2300 °F	Cold Crush Strength
	4.83 MPa @Temperature 1371 °C	700 psi @Temperature 2500 °F	Cold Crush Strength
	4.83 MPa @Treatment Temp. 104 °C	700 psi @Treatment Temp. 219 °F	Cold Crush Strength; Dried 104°C
	6.89 MPa @Treatment Temp. 540 °C	1000 psi @Treatment Temp. 1000 °F	Cold Crush Strength; Dried 104°C

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	1427 °C	2601 °F
Shrinkage	0.20 % @Temperature 540 °C	0.20 % @Temperature 1000 °F	Permanent Linear Change; ASTM C210
	0.20 % @Temperature 815 °C	0.20 % @Temperature 1500 °F	Permanent Linear Change; ASTM C210
	0.20 % @Temperature 1095 °C	0.20 % @Temperature 2003 °F	Permanent Linear Change; ASTM C210
	0.50 % @Temperature 1260 °C	0.50 % @Temperature 2300 °F	Permanent Linear Change; ASTM C210
	2.1 % @Temperature 1371 °C	2.1 % @Temperature 2500 °F	Permanent Linear Change; ASTM C210

Component Elements Properties	Metric	English	Comments
Al2O3	51 %	51 %
CaO	4.7 %	4.7 %
Fe2O3	0.80 %	0.80 %
MgO	0.10 %	0.10 %
Na2O	0.10 %	0.10 %	Includes K<sub>2</sub>O
SiO2	40.1 %	40.1 %
TiO2	1.2 %	1.2 %