- Acrylonitrile Butadiene Styrene (ABS), Molded
- Chi Mei Polylac® PA-756S ABS - High Flow
Chi Mei Polylac® PA-756S ABS - High Flow
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-756S ABS - High Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Super high flow, medium impact
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Melt Flow | 70 g/10 min @Load 10.0 kg, Temperature 220 °C |
70 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 104 MPa | 15100 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ISO 527 |
| Flexural Strength | 61.0 MPa | 8850 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | ISO 179 |
| Impact | 12.0 | 12.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | unannealed; ISO 75 |
| 97.0 °C | 207 °F | annealed; ISO 75 | |
| Vicat Softening Point | 95.0 °C @Load 5.00 kg |
203 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 96.0 °C @Load 5.00 kg |
205 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 102 °C @Load 1.00 kg |
216 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 104 °C @Load 1.00 kg |
219 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 610 BT N 32 C PA610
- PolyOne OnForce™ LFT NN-30LCF/002 Grey Polyamide 66 (Nylon 66)
- Kraton® Cariflex™ IR0401 SU Polyisoprene Rubber Latex
- Mo-Sci Corporation GL-0275-S Class VI Soda-Lime Spheres
- SABIC Innovative Plastics ULTEM 2200R PEI
- Styron XZ 94462.04 Carboxylated SB
- A. Schulman FORMION™ FI 555-31 Recycled Ionomer
- Dow Corning 3715 TOPCOAT
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N330 Filler
Copyright © lookpolymers.com All Rights Reserved