Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 61.0 MPa
8850 psi
ASTM D790-92
Multibase Multi-Pro® 2005 XRC Black 20% Filler Content Polypropylene
Multi-Pro 2005 XRC is specifically designed for injection molded electronic industrial uses. This product shows higher heat distortion and notched izod than typical glass filled polypropylene. Thi..
Flexural Strength 61.0 MPa
8850 psi
Method 1, 0.05"/min; ASTM D790
Proto3000 ABS-M30 Fused Deposition Modeling Polymer
Description: ABS-M30 is up to 25-70 percent stronger than standard Stratasys ABS and is an ideal material for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts. ABS..
Flexural Strength 61.0 MPa
8850 psi
Method 1, 0.05"/min; ASTM D790
Proto3000 ABS-M30i Fused Deposition Modeling Polymer
Description: ABS-M30i is a high strength material well suited for the medical, pharmaceutical and food packaging industries. Parts manufactured with ABS-M30i material are biocompatible (ISO 10993 ce..
Flexural Strength 61.0 MPa
8850 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Europe-Africa-Middle East)
LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength 61.0 MPa
8850 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP AI0019 ABS (Europe-Africa-Middle East)
LNP* Lubricomp* AI0019 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Silicone. Added features of this material include: Flame Retardant.
Flexural Strength 61.0 MPa
8850 psi
ISO 178
Lucite International Diakon® Rapide CLG 910B Enhanced Molding Acrylic Polymer
Specially designed to reduce injection molding cycle times and therefore provide production cost benefits.Information provided by Lucite International
Flexural Strength 61.0 MPa
8850 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DP003EH PC
LNP LUBRICOMP* DP003EH is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Easy Molding, Internally Lubricated, Healthcare.
Flexural Strength 61.0 MPa
8850 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP HH0420A PA11
LNP* HH0420A is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity.
Flexural Strength 61.0 MPa
8850 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KAL22 Acetal Copolymer (Europe-Africa-Middle East)
LNP* Lubricomp* KAL22 is a compound based on Acetal Copolymer resin containing PTFE, Aramid Fiber.
Flexural Strength 61.0 MPa
8850 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific)
LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Flexural Strength 61.0 MPa
8850 psi
ASTM D790
SABIC Innovative Plastics LNP STAT-KON AX00756 ABS
LNP STAT-KON* AX00756 is a compound based on ABS resin containing Stainless Steel. Added feature of this material is: Electrically Conductive.
Flexural Strength 61.0 MPa
8850 psi
ISO 178
SABIC Innovative Plastics LNP STAT-KON RX08408 PA 66
LNP* STAT-KON* RX08404 is a compound based on Nylon 66 containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
Flexural Strength 61.0 MPa
8850 psi
ISO 178
SABIC Innovative Plastics LNP Stat-kon RX08408_NA1D004 PA 66
LNP* Stat-Kon* RX08404_NA1D004 is a compound based on Nylon 66 containing Carbon Powder. Characteristics of this grade include: Electrically Conductive, High Impact.This data was supplied by SABI..
Flexural Strength 61.0 MPa
8850 psi
ISO 178
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific)
LNP* Stat-loy* AF3009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Antistat, Flame Retardant.
Flexural Strength 61.0 MPa
8850 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp FF008L PE
LNP* Thermocomp* FF008L is a compounding based on Polyethylene containing glass fiber. Added characteristics include Low Extractible.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength 61.0 MPa
8850 psi
3-point, 2 mm/min; ISO 178
Styron MAGNUMâ„¢ 3325 SLG Acrylonitrile Butadiene Styrene (ABS) Resin
Overview: Super Low Gloss, Medium Heat, Medium Impact ABS resin for injection molded automotive interior trim applications Magnum 3325 SLG can achieve 60° Gardner gloss levels below 2.0 with low ..
Flexural Strength 61.0 MPa
8850 psi
ISO 178
SABIC Innovative Plastics LNP STAT-LOY W3000XXJ PBT
LNP* STAT-LOY* W3000XXJ is a compound based on PBT. Added features of this grade include: Anti-Stat, Colorable, Healthcare
Flexural Strength 61.0 MPa
8850 psi
ASTM D790
Stratasys® ABSi
Stratasys is the only company that gives engineers the ability to manufacture real ABSi industrial thermoplastic parts direct from digital files. ABSi parts can be used from conceptual prototyping t..
Flexural Strength 61.0 MPa
8850 psi
Method 1, .05"/min; ASTM D790
Stratasys® ABS-M30
ABS-M30 is 25-70 percent stronger than standard Stratasys ABS and is an ideal material for conceptual prototyping, design verification, and direct digital manufacturing. ABS-M30 has greater tensile,..
Flexural Strength 61.0 MPa
8850 psi
2 mm/min; ISO 178
Chi Mei Polylac® PA-747R ABS - Extrusion
Attach case and refrigerator
Flexural Strength 61.0 MPa
8850 psi
2 mm/min; ISO 178
Chi Mei Polylac® PA-756S ABS - High Flow
Super high flow, medium impact
Flexural Strength 61.0 MPa
8850 psi
ISO 178
Azoty Tarnow™ TARNOFORM 300 LS POM
Injection molding grade based on Tarnoform 300 modified with soluble light stabilizers improving weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Flexural Strength 61.0 MPa
8850 psi
ISO 178
Azoty Tarnow™ TARNOFORM 300 POM
Basic, fast cycling injection molding grade suitable for many applications.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Flexural Strength 61.0 MPa
8850 psi
ISO 178
Azoty Tarnow™ TARNOFORM 300 UV POM
Injection molding grade based on Tarnoform 300 modified with carbon black giving best weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Flexural Strength 61.0 MPa
8850 psi
ISO 178
Azoty Tarnow™ TARNOFORM 500 UV POM
High flow injection molding grade based on Tarnoform 500 modified with carbon black giving best weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Flexural Strength 61.0 MPa
8850 psi
ASTM D790
A. Schulman ComAlloy Comtuf® 420 Polyester - PBT, High Impact Modified
Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc..
Flexural Strength 61.0 MPa
8850 psi
ASTM D790
Aclo Accutech Polypropylene Copolymer CP0436G20M10CL Glass/Mineral Reinforced Coupled
Flexural Strength 61.0 MPa
8850 psi
ASTM D790
Ineos Nova Zylar® 631 Clear Impact Modified Acrylic Copolymer  (discontinued **)
Features:Outstanding practical toughness and ductilityStyrenic processing advantagesExcellent property retention after ETO and gamma sterilizationUSP Class VI compliantCustom colors and enhancement ..
Flexural Strength 61.0 MPa
8850 psi
ASTM D790
Plenco 7321 Phenolic, Nodular, Injection Molded
PLENCO 07321 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength and excellent dimensional stability. Type ASTM 5948 CFI-5, and UL recognized under compon..
Flexural Strength 61.0 MPa
8850 psi
ISO 178
Polyplastics Duracon® SF-10 Acetal Co-polymer (POM), High impact, Flexible
DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..