Chesterton ARC I BX1 Impact & Wear Resistant Epoxy Composite

Category Polymer , Thermoset , Epoxy
Manufacturer Chesterton
Trade Name ARC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chesterton ARC I BX1 Impact & Wear Resistant Epoxy Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: An advanced grade epoxy and urethane composite for the repair and protection of all metal surfaces subjected to severe abrasion and impact. It is normally applied at a thickness of 6 mm(1/4”) or more. Non-shrinking. 100% Solids. ARC I BX1 is formulated with a high concentration of ceramic beads, fine ceramic particles and urethane for extremely abrasive and impactful environments where metal loss is often repaired by more conventional and costly weld overlay. It can be used either to rebuild eroded metal surfaces or provide a wear resistant surface, which frequently outperforms the original metal, weld overlay, rubber liners or ceramic tiles.Benefits:Excellent wear characteristics extends equipment operating cycles, typically outwears weld overlay or ceramic tilesTough resin structure resists thermal-mechanical shockOutstanding adhesion results in reliable performanceLabor and downtime costs are reduced due to ease of applicationPerforms well under fluctuation chemical environments, unlike metals which are sensitive to environmental changesConvenient packaging suitable for large volume applicationsResistant in direct impact applicationsAbsorbs impact Suggested Uses:Hoppers/ChutesHydro PulpersNi-hard Slurry PumpsPneumatic ConveyorsTurbo SeparatorsPulverizers and Impact ZonesWear PlatesPipe ElbowsPulverized Fuel LinesScrew ConveyoursInformation provided by Chesterton
Physical Properties Metric English Comments
Density 2.40 g/cc
0.0867 lb/in³
Cured
Mechanical Properties Metric English Comments
Hardness, Shore D 83
83
ASTM D2240
Tensile Strength at Break 19.0 MPa
2750 psi
ASTM D638
Elongation at Break 1.7 %
1.7 %
ASTM D638
Flexural Strength 30.5 MPa
4420 psi
ASTM D790
Flexural Modulus 4.96 GPa
720 ksi
ASTM C580
Compressive Strength 47.1 MPa
6830 psi
ASTM D695
Adhesive Bond Strength >= 13.8 MPa
>= 2000 psi
ASTM D4541
Impact Test 20.3 J
15.0 ft-lb
Reverse; ASTM D2794
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 95.0 °C
203 °F
Wet Service
205 °C
401 °F
Dry Service
Processing Properties Metric English Comments
Cure Time 30.0 min

@Temperature 43.0 °C
0.500 hour

@Temperature 109 °F
Tack Free
90.0 min

@Temperature 43.0 °C
1.50 hour

@Temperature 109 °F
Light Load
120 min

@Temperature 32.0 °C
2.00 hour

@Temperature 89.6 °F
Tack Free
240 min

@Temperature 25.0 °C
4.00 hour

@Temperature 77.0 °F
Tack Free
360 min

@Temperature 32.0 °C
6.00 hour

@Temperature 89.6 °F
Light Load
420 min

@Temperature 16.0 °C
7.00 hour

@Temperature 60.8 °F
Tack Free
480 min

@Temperature 25.0 °C
8.00 hour

@Temperature 77.0 °F
Light Load
720 min

@Temperature 43.0 °C
12.0 hour

@Temperature 109 °F
Full Load
1200 min

@Temperature 32.0 °C
20.0 hour

@Temperature 89.6 °F
Full Load
1440 min

@Temperature 16.0 °C
24.0 hour

@Temperature 60.8 °F
Light Load
1440 min

@Temperature 43.0 °C
24.0 hour

@Temperature 109 °F
Full Chemical
1800 min

@Temperature 25.0 °C
30.0 hour

@Temperature 77.0 °F
Full Load
1800 min

@Temperature 32.0 °C
30.0 hour

@Temperature 89.6 °F
Full Chemical
2160 min

@Temperature 25.0 °C
36.0 hour

@Temperature 77.0 °F
Full Chemical
2880 min

@Temperature 16.0 °C
48.0 hour

@Temperature 60.8 °F
Full Load
4320 min

@Temperature 16.0 °C
72.0 hour

@Temperature 60.8 °F
Full Chemical
Descriptive Properties Value Comments
Color Gray