CeramTec Ceramtape GC Glass Ceramic

Category	Ceramic , Glass , Glass Ceramic
Manufacturer	CeramTec North America
Trade Name	Ceramtape
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	CeramTec Ceramtape GC Glass Ceramic.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LTCC (Low Temperature Cofired Ceramic) is a new type of ceramic film developed by CeramTec AG's Electronics division. With the aid of these ceramics and their almost shrinkage-free sintering process, highly complex multilayer assemblies for electronic applications are possible. Apart from the automotive sector, LTCC is also ideally suited for the up-and-coming Bluetooth applications, medical apparatus, and consumer electronics. In the automotive sector, it is used for motor-management and ABS-systems. Ceramtape GC is a glass ceramic made of alumina and anorthite.

Physical Properties	Metric	English	Comments
Bulk Density	1.63 - 1.93 g/cc	0.0589 - 0.0697 lb/in³	Green
Density	2.87 - 2.97 g/cc	0.104 - 0.107 lb/in³	Fired
Thickness	40.0 - 60.0 microns	1.57 - 2.36 mil	PET
	324 - 396 microns	12.8 - 15.6 mil	Blank on PET

Mechanical Properties	Metric	English	Comments
Flexural Strength	>= 170 MPa	>= 24700 psi

Thermal Properties	Metric	English	Comments
CTE, linear	4.90 - 5.70 µm/m-°C	2.72 - 3.17 µin/in-°F
Thermal Conductivity	1.20 - 3.20 W/m-K	8.33 - 22.2 BTU-in/hr-ft²-°F
Shrinkage	17.5 - 18.5 %	17.5 - 18.5 %	2-layer Laminate; z-direction
	20.5 - 21.5 %	20.5 - 21.5 %	2-layer Laminate; x-direction
	20.9 - 21.9 %	20.9 - 21.9 %	2-layer Laminate; y-direction

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+14 ohm-cm	>= 1.00e+14 ohm-cm
Dielectric Constant	7.3 - 8.5 @Frequency 1.00e+6 Hz	7.3 - 8.5 @Frequency 1.00e+6 Hz
Dielectric Strength	>= 100 kV/mm	>= 2540 kV/in
Dissipation Factor	<= 0.0020 @Frequency 1.00e+6 Hz	<= 0.0020 @Frequency 1.00e+6 Hz	tand

Descriptive Properties	Value	Comments
Cooling Rate (K/min)	1 to 6	Firing Conditions
Dwell Time at Peak Temperature (min)	10 to 40	Firing Conditions
Heating Rate (K/min)	1 to 4	Firing Conditions
Laminating Pressure (kg/cm³)	50-130
Laminating Temperature (°C)	30-80
Laminating Time (min)	0.5-3
Peak Temperature (°C)	880-920	Firing Conditions