Braskem HF 0150 HDPE Blown Film Extrusion Polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Braskem
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem HF 0150 HDPE Blown Film Extrusion Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Grocery and T-shirt bags; merchandise bags; frozen-food bags. Information provided by Braskem
Physical Properties Metric English Comments
Density 0.948 g/cc
0.0342 lb/in³
ASTM D1505
Thickness 38.0 microns
1.50 mil
Melt Flow 0.45 g/10 min

@Load 5.00 kg,
Temperature 190 °C
0.45 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ASTM D1238
High Load Melt Index 10 g/10 min

@Load 21.6 kg,
Temperature 190 °C
10 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 23.0 MPa
3340 psi
ASTM D882
Film Tensile Strength at Yield, TD 27.0 MPa
3920 psi
ASTM D882
Film Elongation at Break, MD 571 %
571 %
ASTM D882
Film Elongation at Break, TD 832 %
832 %
ASTM D882
Elmendorf Tear Strength, MD 0.600 g/micron
15.2 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 4.10 g/micron
104 g/mil
ASTM D1922
Dart Drop 3.13 g/micron
79.5 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 57.0 MPa
8270 psi
ASTM D882
Film Tensile Strength at Break, TD 54.0 MPa
7830 psi
ASTM D882
Heat Seal Strength Initiation Temperature 125 °C
257 °F
Sealing Initial Temperature; Braskem® Method
Descriptive Properties Value Comments
Minimum Recommended Thickness 13 µm
Puncture Strength 71 J/m
Braskem® Method