Polymer Property : Film Tensile Strength at Break, MD = 57.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	57.0 MPa	8270 psi	ASTM D 882
NOVA Chemicals Sclair® FP020-D Octene Copolymer LLDPE Film Resin FP020-D complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. FP020..
Film Tensile Strength at Break, MD	57.0 MPa	8270 psi	ASTM D882
Eastman Eastar 5445 PCTG Copolyester, Film (discontinued **) Eastar PCTG 5445 is an amorphous copolyester. Because of its clarity, toughness and good melt strength, Eastar PCTG Copolyester 5445 is useful in a number of applications. It has high gloss and is t..
Film Tensile Strength at Break, MD	57.0 MPa	8270 psi	ASTM D882
ExxonMobil Exceed™ 350D60 LDPE/Hexene Tough Premium Film Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 350D60 resin have outstanding tensile, impact streng..
Film Tensile Strength at Break, MD	57.0 MPa	8270 psi	Orientation not specified; ASTM D882
EVALCA EVAL® EP-J102B Ethylene Vinyl Alcohol Copolymer Resin (discontinued **) 32 mol % Ethylene.Data provided by EVALCA. Designed to provide a wide thermoforming range together with high barrier properties. EVAL® EP-J102B is specifically designed for thermoforming applicat..
Film Tensile Strength at Break, MD	57.0 MPa	8270 psi	ASTM D882
Solvay Specialty Polymers Ajediumâ„¢ PVDF 9009 Polyvinylidene Fluoride (PVDF) SolefÂ® 9009 PVDF homopolymer is a semi-crystalline fluoropolymer. SolefÂ® film is chemically inert to most acids, aliphatic and aromatic organic compounds, chlorinated solvents and alcohols.Fea..
Film Tensile Strength at Break, MD	57.0 MPa	8270 psi	ISO 527-3
Borealis Borstar® FB1350 Medium Density Polyethylene Borstar® FB1350 is a linear medium density polyethylene grade combining excellent extrusion properties with high film stiffness. Borstar® FB1350 is well suited for mono- and coextrusion of films ..
Film Tensile Strength at Break, MD	57.0 MPa	8270 psi	ISO 527-3
Topas Advanced Polymers TOPAS® 8007F-04 Cyclic Olefin Copolymer (COC) TOPAS® 8007F-04 is a general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and..
Film Tensile Strength at Break, MD	57.0 MPa	8270 psi	ISO 527-3
Total Lumicene® mPE M5510 EP Metallocene Polyethylene, Blown Film This product is a Total Ecosolutions grade.Lumicene® mPE M5510 EP is a second generation metallocene high density homopolymer polyethylene.Lumicene® mPE M5510 EP can be processed at high output ra..
Film Tensile Strength at Break, MD	57.0 MPa	8270 psi	ASTM D882
Eastman Tritan FX200 Copolyester Eastman Tritan FX200 is an amorphous copolyester that combines clarity and toughness with heat and chemical resistance. Films manufactured from this new-generation copolyester can be thermoformed w..
Film Tensile Strength at Break, MD	57.0 MPa	8270 psi	ASTM D882
Braskem HF 0150 HDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Grocery and T-shirt bags; merchandise bags; frozen-food bags. Information provided by Bras..
Film Tensile Strength at Break, MD	57.0 MPa	8270 psi	ASTM D882
Braskem LQ 0518/30 LLDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Heavy duty bags; shrink film. Information provided by Braskem