SABIC Innovative Plastics LNP STAT-KON LX00797C PEEK

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON LX00797C PEEK.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* LX00797C is a compound based on Polyetheretherketone containing Proprietary Filler(s). Added features of this material include: ristics of this grade are: Clean Compounding System, Electrically Conductive.
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D792
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Mechanical Properties Metric English Comments
Tensile Strength at Break 155 MPa
22500 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.5 %
2.5 %
Type I, 5 mm/min; ASTM D638
Flexural Strength 195 MPa
28300 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 7.92 GPa
1150 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.70 J/cm
5.06 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 310 °C

@Thickness 3.20 mm
590 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1000 - 1.00e+6 ohm-cm
1000 - 1.00e+6 ohm-cm
ASTM D257
Surface Resistance 1000 - 1.00e+6 ohm
1000 - 1.00e+6 ohm
ASTM D257