Borealis Daplen™ ED206HP TPO Compound

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polypropylene (PP) , TPO
Manufacturer Borealis
Trade Name Daplen™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ ED206HP TPO Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen ED206HP is a 25% mineral reinforced compound intended for injection molding. ED206HP has been developed especially for the car industry, to be used in interior parts requiring excellent scratch resistance. ED206HP has good processability with optimized physical properties.Daplen ED205HP has been developed especially for dashboards, interior panels, dashboard inserts, door panels and pockets, and consoles.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Borealis Method
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
30 g/10 min

@Load 5.00 kg,
Temperature 230 °C
30 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 50
50
ISO 868
Ball Indentation Hardness 35.0 MPa
5080 psi
H385/30; ISO 2039
Tensile Strength, Yield 20.0 MPa
2900 psi
At 50 mm/min; ISO 527-2
Flexural Strength 20.0 MPa
2900 psi
ISO 178
Flexural Modulus 1.92 GPa
278 ksi
At 2 mm/min; ISO 527-2
Charpy Impact Unnotched NB
NB
ISO 179/1eU
6.20 J/cm²

@Temperature -20.0 °C
29.5 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.520 J/cm²

@Temperature -20.0 °C
2.47 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 120 °C
248 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO 75-2
Vicat Softening Point 56.0 °C
133 °F
B (50N); ISO 306
135 °C
275 °F
A (10N); ISO 306
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Mold Temperature 30.0 - 60.0 °C
86.0 - 140 °F
Descriptive Properties Value Comments
Emissions, ug C/g 24
VDA 277
Fogging % 98
At 100°C/3 hours
Fogging, mg 0.4
At 100°C/ 16 hours