BASF Capron® 8351 HS BK-102 Impact Modified Nylon 6 (Dry)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 8351 HS BK-102 Impact Modified Nylon 6 (Dry)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 8351 HS BK-102 is a heat stabilized, pigmented black type 6 nylon graft copolymer developed for injection molding applications requiring a high level of toughness combined with a moderate flexibility and faster cycles. Excellent thermal and chemical resistance properties provided by the polyamide backbone. It demonstrates the highest impact performance within the Capron copolymer product line while maintaining an excellent balance of strength and stiffness. Excellent chemical resistance to greases, oils and hydrocarbons.Capron 8351 HS Bk-102 is generally recommended for applications such as spray gun and power tool handles, trim clips and fasteners, wall anchors and automotive roof clips rack components. ASTM Callout PA263 + PA0220 B32310.Data provided by Allied Signal.Processing: Max. water content 0.2%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 240-270 degC (464-518 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) A mold temperature of 80-95 degC (176-203 degF) is recommended, but temperatures of 10-95 degC (50-203 degF) can be used where applicable. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO data
Water Absorption 1.1 %
1.1 %
24 hrs; ISO data
Moisture Absorption at Equilibrium 1.9 %
1.9 %
50% RH; 23°C; ISO data
Water Absorption at Saturation 6.7 %
6.7 %
in water; 23°C; ISO data
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ISO data
0.014 cm/cm
0.014 in/in
ASTM data MD
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO Data
Mechanical Properties Metric English Comments
Tensile Strength, Yield 53.0 MPa
7690 psi
ISO value at 50 mm/min.
55.0 MPa
7980 psi
ASTM value at 50 mm/min.
Elongation at Break >= 50 %
>= 50 %
Nominal
>= 100 %
>= 100 %
Nominal
Flexural Modulus 1.40 GPa
203 ksi
ISO Value
1.69 GPa
245 ksi
ASTM Value
Poissons Ratio 0.35
0.35
ISO data
Thermal Properties Metric English Comments
CTE, linear 106 µm/m-°C

@Temperature 20.0 °C
58.9 µin/in-°F

@Temperature 68.0 °F
ASTM data
Melting Point 220 °C
428 °F
ASTM and ISO test
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
ASTM Data
Flammability, UL94 HB

@Thickness 0.810 mm
HB

@Thickness 0.0319 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ISO data
Processing Properties Metric English Comments
Processing Temperature 275 °C
527 °F
See Materials Notes
Mold Temperature 95.0 °C
203 °F
See Materials Notes
Drying Temperature 85.0 °C
185 °F
See Materials Notes