Alliance Polymers Viprene™ G90A-32U-NAT Thermoplastic Vulcanizate Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV)
Manufacturer Alliance Polymers
Trade Name Viprene™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Alliance Polymers Viprene™ G90A-32U-NAT Thermoplastic Vulcanizate Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Viprene™ G90A-32U-NAT is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing characteristics. Availability: North AmericaAdditive: Heat Stabilizer and UV StabilizerFeatures: Good Flow, Good UV Resistance and Heat StabilizedAppearance: Natural ColorForms: PelletsProcessing Method: Extrusion and Injection MoldingInformation provided by Alliance Polymers
Physical Properties Metric English Comments
Density 0.950 g/cc
0.0343 lb/in³
ISO 2781
Mechanical Properties Metric English Comments
Hardness, Shore A 90
90
ISO 868
Hardness, Shore D 38
38
ISO 868
Tensile Strength at Break 12.4 MPa
1800 psi
ISO 37
Tensile Stress 7.31 MPa

@Strain 100 %
1060 psi

@Strain 100 %
ISO 37
9.58 MPa

@Strain 300 %
1390 psi

@Strain 300 %
ISO 37
Elongation at Break 500 %
500 %
ISO 37
Tear Strength 57.8 kN/m
330 pli
ISO 34-1
Compression Set 49 %

@Temperature 70.0 °C,
Time 79200 sec
49 %

@Temperature 158 °F,
Time 22.0 hour
ASTM D3995B
Thermal Properties Metric English Comments
Brittleness Temperature -60.0 °C
-76.0 °F
ASTM D746
Flammability, UL94 HB

@Thickness 1.00 mm
HB

@Thickness 0.0394 in
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Processing Properties Metric English Comments
Processing Temperature 205 °C
401 °F
Gate Temperature; Extrusion
200 - 230 °C
392 - 446 °F
Injection
Rear Barrel Temperature 185 °C
365 °F
Injection
Middle Barrel Temperature 190 °C
374 °F
Injection
Front Barrel Temperature 195 °C
383 °F
Injection
Nozzle Temperature 195 - 225 °C
383 - 437 °F
Injection
Zone 1 185 °C
365 °F
Extrusion
Zone 2 195 °C
383 °F
Extrusion
Zone 3 200 °C
392 °F
Extrusion
Die Temperature 210 °C

@Pressure 4.80 - 17.0 MPa
410 °F

@Pressure 696 - 2470 psi
Extrusion
Mold Temperature 10.0 - 50.0 °C
50.0 - 122 °F
Injection
Injection Velocity >= 50.0 mm/sec
>= 1.97 in/sec
Injection
Drying Temperature 80.0 °C
176 °F
Injection
80.0 °C
176 °F
Extrusion
Dry Time 3.00 hour
3.00 hour
Injection
3.00 hour
3.00 hour
Extrusion
Back Pressure 0.400 - 0.800 MPa
58.0 - 116 psi
Injection
Clamp Pressure 40.0 - 70.3 MPa
5800 - 10200 psi
Injection
Screw Speed 100 - 200 rpm
100 - 200 rpm
Injection