Polymer Resources PC/TP-GP3-G30 PC/Polyester Alloy, 30% Glass Reinforced

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend, Glass Reinforced , Polyester, TP
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC/TP-GP3-G30 PC/Polyester Alloy, 30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Superior Chemical Resistance, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.44 g/cc
1.44 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 1.0 - 8.0 g/10 min

@Load 2.16 kg,
Temperature 265 °C
1.0 - 8.0 g/10 min

@Load 4.76 lb,
Temperature 509 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 89.6 MPa
13000 psi
ASTM D638
Tensile Strength, Yield 89.6 MPa
13000 psi
ASTM D638
Flexural Strength 134 MPa
19500 psi
ASTM D790
Flexural Modulus 5.34 GPa
775 ksi
ASTM D790
Izod Impact, Notched 1.44 J/cm

@Temperature 22.8 °C
2.70 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 199 °C
390 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 143 °C
290 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Processing Properties Metric English Comments
Rear Barrel Temperature 249 - 271 °C
480 - 520 °F
Middle Barrel Temperature 254 - 277 °C
490 - 530 °F
Front Barrel Temperature 260 - 282 °C
500 - 540 °F
Melt Temperature 260 - 288 °C
500 - 550 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Descriptive Properties Value Comments
Vent 0.0015