ExxonMobil Exceed™ 377D60 LDPE/Hexene Tough Premium Film Resin, 3 mil Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 377D60 LDPE/Hexene Tough Premium Film Resin, 3 mil Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 377D60 resin exhibit excellent impact strength and balanced tensile and tear.Applications: Shipping sacks; Heavy duty bags; Trash bag; Liners; General packaging. Data for film properties below based on 3 mil film.
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
Exxon Method
Thickness 76.2 microns
3.00 mil
Melt Flow 1.0 g/10 min
1.0 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.3 MPa
1640 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.9 MPa
1730 psi
ASTM D882
Film Elongation at Break, MD 630 %
630 %
ASTM D882
Film Elongation at Break, TD 640 %
640 %
ASTM D882
Secant Modulus, MD 0.293 GPa
42.5 ksi
ASTM D882
Secant Modulus, TD 0.317 GPa
46.0 ksi
ASTM D882
Coefficient of Friction 0.62
0.62
ASTM D1894
Elmendorf Tear Strength MD 970 g
970 g
ASTM D1922
Elmendorf Tear Strength TD 1240 g
1240 g
ASTM D1922
Elmendorf Tear Strength, MD 12.7 g/micron
323 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 16.3 g/micron
413 g/mil
ASTM D1922
Dart Drop 9.96 g/micron
253 g/mil
F50; ASTM D1709
Dart Drop Test 760 g
1.68 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 50.0 MPa
7250 psi
ASTM D882
Film Tensile Strength at Break, TD 49.0 MPa
7110 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 120 °C
248 °F
Exxon Method