Multibase Multi-Flex® A 8502 LC TPE Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® A 8502 LC TPE Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Chemical Resistance, Good Thermal Stability, GoodOzone Resistant Forms:PelletsProcessing Method:Injection MoldingExtrusion Uses: Automotive Interior PartsInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM 792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 83 | 83 | 10 seconds; ASTM D2240 |
| Tensile Strength, Yield | 4.55 MPa | 660 psi | at 100% secant; ASTM D638 |
| 11.0 MPa | 1600 psi | Elastic; ASTM D638 | |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 0.0586 GPa | 8.50 ksi | ASTM D790 |
| Tear Strength | 43.8 kN/m | 250 pli | ASTM D624 |
| Compression Set | 25 % | 25 % | 73°F, 70 hours; ASTM D395 |
| 51 % | 51 % | 158°F, 70 hours; ASTM D395 |