NOVA Chemicals Novapol® PF-0118-DP Butene Copolymer LLDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer NOVA Chemicals
Trade Name Novapol®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® PF-0118-DP Butene Copolymer LLDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PF-0118-DP complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food, without temperature or food-type restrictions, subject to technical suitability. It is also biologically and chemically inert.The NOVA Chemicals Material Safety Data Sheet contains important safety information and should be reviewed before using the product.Features: Toughness and strengthAdditives: Process stabilizer, High slip and antiblock, Process aidApplications: Trash bags, garment film, bags-on-roll, linersFilm properties are typical of blown film extruded on a 2.5" extruder with 4" die and 100-mil die gap at a blow up ratio of 2.5:1, but are dependent upon operating conditions.
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ASTM D 792
Thickness 25.0 microns
0.984 mil
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D 882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D 882
Film Elongation at Break, MD 540 %
540 %
ASTM D 882
Film Elongation at Break, TD 830 %
830 %
ASTM D 882
Elmendorf Tear Strength MD 100 g
100 g
ASTM D 1922
Elmendorf Tear Strength TD 330 g
330 g
ASTM D 1922
Elmendorf Tear Strength, MD 4.00 g/micron
102 g/mil
ASTM D 1922
Elmendorf Tear Strength, TD 13.2 g/micron
335 g/mil
ASTM D 1922
Dart Drop 4.00 g/micron
102 g/mil
F50; ASTM D 1709/A
Dart Drop Test 100 g
0.221 lb
F50; ASTM D 1709/A
Film Tensile Strength at Break, MD 49.0 MPa
7110 psi
ASTM D 882
Film Tensile Strength at Break, TD 34.0 MPa
4930 psi
ASTM D 882
1% Secant Modulus, MD 200 MPa
29000 psi
ASTM D 882
1% Secant Modulus, TD 230 MPa
33400 psi
ASTM D 882
Optical Properties Metric English Comments
Haze 11 %
11 %
ASTM D 1003
Gloss 56 %
56 %
45°; ASTM D 2457
Processing Properties Metric English Comments
Melt Temperature 195 - 220 °C
383 - 428 °F
Die Opening 0.0900 - 0.220 cm
0.0354 - 0.0866 in
Blow-up Ratio (BUR) 2.0 - 3.0
2.0 - 3.0
Optimum
Descriptive Properties Value Comments
Low Friction Puncture 34 (J/mm)
NOVA Chemicals test method