Polymer Property : Melt Flow = 3.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 1.0 - 3.0 g/10 min
1.0 - 3.0 g/10 min
(Condition L) ASTM D-1238
Multibase Multi-Flex® TPE G 7680 NAT
The burn rate is 1.2 in/min (30 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Melt Flow 1.0 - 3.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 - 3.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Polyplastic Armobond® PE 2K Polyethylene Adhesive Compound
Information provided by PolyPlastic Group.
Melt Flow 2.0 - 3.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
2.0 - 3.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
NIZHNEKAMSKNEFTEKHIM 825E High Impact Polystyrene
Grade 825E is a high impact polystyrene designed specifically for extrusion and thermoforming. It is used for production of industrial packaging via deep draw thermoforming and custom multilayer sh..
Melt Flow 1.0 - 3.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 - 3.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Polymer Resources AH-GP1 Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Melt Flow 1.0 - 3.0 g/10 min
1.0 - 3.0 g/10 min
ASTM D1238
Polymer Resources AH-GP1-[color]-H Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 1.0 - 3.0 g/10 min

@Load 11.6 kg,
Temperature 250 °C
1.0 - 3.0 g/10 min

@Load 25.6 lb,
Temperature 482 °F
ASTM D1238
Polymer Resources PPX-FR6 Modified-PPO, V-0 Flame Retardant
Modified-Polyphenylene Oxide, V-0 Flame Retardant, 300F HDTFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-..
Melt Flow 2.0 - 3.0 g/10 min
2.0 - 3.0 g/10 min
ASTM D1238
Plaskolite West Optix® CA-81 UVA-7 UV-Absorbing Acrylic Resin
Special UV-absorption grade, extrusion and injection moldingApplications: A special UV-absorption acrylic resin for extrusion and injection molding. It is slightly lubricated for ease of processing..
Melt Flow 0.30 - 3.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.30 - 3.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Polymer Resources AC-G25 Acetal Copolymer, 25% Glass Reinforced
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Melt Flow 0.20 - 3.0 g/10 min
0.20 - 3.0 g/10 min
on the basis of basic grades 10703-020, 10803-020, and 18503-020, for masterbatches of other applications (coloring general purpose products, coloring toys, coloring food containers
Kazanorgsintez P2KP Polyethylene Pigment Masterbatches
Production Method: P2KP polyethylene pigment masterbatches are produced on the basis of low density polyethylene with high content of masterbatches. Application: P2KP polyethylene pigment masterbatc..
Melt Flow 1.0 - 3.0 g/10 min
1.0 - 3.0 g/10 min
on the basis of basic grades 10703-020, 10803-020, and 18503-020, for cable masterbatches
Kazanorgsintez P2KP Polyethylene Pigment Masterbatches
Production Method: P2KP polyethylene pigment masterbatches are produced on the basis of low density polyethylene with high content of masterbatches. Application: P2KP polyethylene pigment masterbatc..
Melt Flow 2.0 - 3.0 g/10 min

@Load 5.00 kg,
Temperature 190 °C
2.0 - 3.0 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
FKuR Kunststoff Fibrolon® P 8540 Wood-Plastic Compound, Fiber Reinforced
FIBROLON® are fiber reinforced compounds. Fibrolon® P 8540 has a polypropylene base. With the brand name of FIBROLON® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-C..
Melt Flow 2.4 - 3.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.4 - 3.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
FKuR Kunststoff Terralene® LL 1303 Biobased Polyethylene
With the brand name Terralene® FKuR offers biobased polyethylene compounds made using Braskem's Green PE. When compared to conventional polyethylene (PE), the main difference is that the ethanol..
Melt Flow 1.5 - 3.0 g/10 min

@Load 5.00 kg,
Temperature 372 °C
1.5 - 3.0 g/10 min

@Load 11.0 lb,
Temperature 702 °F
ASTM D1238
Solvay Specialty Polymers Hyflon® PFA 125 Perfluoroalkoxy (PFA)
Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat res..
Melt Flow 1.5 - 3.0 g/10 min

@Load 5.00 kg,
Temperature 372 °C
1.5 - 3.0 g/10 min

@Load 11.0 lb,
Temperature 702 °F
ASTM D1238
Solvay Specialty Polymers Hyflon® PFA 420 Perfluoroalkoxy (PFA)
Hyflon® PFA is a family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resistance..
Melt Flow 1.0 - 3.0 g/10 min
1.0 - 3.0 g/10 min
190/2.16; May be specified; ASTM D1238
Plastics Group Polifil® RP-LDPE Low Density Polyethylene
Polifil® RP-Low Density Polyethylene is a soft, tough material with good clarity and high chemical resistance. LDPE remains flexible and retains impact strength at very low temperatures. High melt ..
Melt Flow 1.0 - 3.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 - 3.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Unitika TERRAMAC HV-6250H Polylactic Acid (PLA)
Foam, Extrusion, blow, and foam sheet grades. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd.
Melt Flow 2.0 - 3.0 g/10 min

@Load 5.00 kg,
Temperature 372 °C
2.0 - 3.0 g/10 min

@Load 11.0 lb,
Temperature 702 °F
Daikin NEOFLON NP-130 FEP Pellets
NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion.Applications: Heavy wall wire insulation, cable jacketing, pipe, shrinka..
Melt Flow 2.0 - 3.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 - 3.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Breplast Bretene HD Caps Flakes High Density Polyethylene
Recovered polyethylene compositeInformation provided by Breplast S.p.A.
Melt Flow 2.0 - 3.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 - 3.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Breplast Bretene HDT High Density Polyethylene
Recovered polyethylene compositeInformation provided by Breplast S.p.A.
Melt Flow 1.0 - 3.0 g/10 min
1.0 - 3.0 g/10 min
Asahi Glass Fluon® P-66P PFA Perfluoropolymer
Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character..
Melt Flow 1.0 - 3.0 g/10 min
1.0 - 3.0 g/10 min
Asahi Glass Fluon® P-802UP PFA Perfluoropolymer
Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character..
Melt Flow 1.5 - 3.0 g/10 min

@Load 5.00 kg,
Temperature 372 °C
1.5 - 3.0 g/10 min

@Load 11.0 lb,
Temperature 702 °F
ASTM D1238
Solvay Specialty Polymers Hyflon® PFA 420 Perfluoroalkoxy (PFA)  (Unverified Data**)
Hyflon® PFA is a family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resistance, ..
Melt Flow 1.0 - 3.0 g/10 min
1.0 - 3.0 g/10 min
ASTM D1238
Polymer Resources AH-GP1 Acetal Homopolymer, Low Flow, High Melt Strength  (Unverified Data**)
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 2.5 - 3.0 g/10 min
2.5 - 3.0 g/10 min
Ashley Polymers Ashlene® RH180 Acetal
Extrusion grade reprocessed homopolymer, excellent toughness, strength, stiffness and lubricity. Available in Natural and Black. Natural is designated RH180; Black is designated RH180B.Data provid..
Melt Flow 1.0 - 3.0 g/10 min
1.0 - 3.0 g/10 min
ASTM D1238
Polymer Resources PPX-FR6 Modified PPO, UL 94 V-0 with HDT of 300 F  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.