Styrolution Novodur® E309 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Novodur® E309 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Novodur E309 is a extrusion grade especially designed for furniture profilesInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 95.0 MPa | 13800 psi | ISO 2039-1 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | ISO 527 |
| Elongation at Yield | 2.7 % | 2.7 % | ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527 |
| Flexural Strength | 65.0 MPa | 9430 psi | ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 21.0 kJ/m² @Temperature 23.0 °C |
9.99 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 14.0 J/cm² @Temperature 23.0 °C |
66.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 2.20 J/cm² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75 |
| Vicat Softening Point | 100 °C @Load 5.10 kg |
212 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | ISO 294 |
| Mold Temperature | 70.0 °C | 158 °F | ISO 294 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- LG Chemical LUPOY NS5000 PC/ABS, High Impact
- Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes
- Sax Polymers SAXAMID 136Q32 Nylon 6, Injection Molding Grade
- Styron DL 233NA Functionalized SB
- Corning Macor® Machinable Glass Ceramic
- ChevronTexaco Starguide™ ISO 46
- Asahi Kasei Thermylene® P6-10FG-0600 10% Glass Fiber Reinforced, Heat Stabilized
- 3M Scotchcal™ ElectroCut™ 7725-17 Graphic Film
- PolyOne Edgetek® NI-20GF/000 Nylon 6/10, Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved