Styrolution Luran® S KR 2859 ASA
| Category | Polymer , Thermoplastic , ASA Polymer |
| Manufacturer | Styrolution |
| Trade Name | Luran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Luran® S KR 2859 ASA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Stiff extrusions product, versatile grade for profile and sheet extrusion as protective cap layer.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Water Absorption | 1.65 % | 1.65 % | Equilibrium; ISO 62 |
| 0.45 % @Time 86400 sec |
0.45 % @Time 24.0 hour |
ISO 62 | |
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | 23°C/50% RH; ISO 62 |
| Melt Flow | 12.84 g/10 min @Load 10.0 kg, Temperature 220 °C |
12.84 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527-1/-2 |
| Elongation at Break | 7.0 % | 7.0 % | Nominal, 50 mm/min; ISO 527-1/-2 |
| Elongation at Yield | 3.2 % | 3.2 % | 50 mm/min; ISO 527-1/-2 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 16.0 J/cm² @Temperature 23.0 °C |
76.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 1200 MPa @Strain <=0.500 % |
174000 psi @Strain <=0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 - 110 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.4 - 61.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| Vicat Softening Point | 98.0 °C | 208 °F | VST/B/50; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | Extrusion, Pipes |
| 210 - 230 °C | 410 - 446 °F | Blow Molding | |
| 230 - 270 °C | 446 - 518 °F | Extrusion, Plates | |
| Mold Temperature | 60.0 °C | 140 °F | Blow molding |
| Drying Temperature | 80.0 °C | 176 °F | Pre-drying |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Pre-drying |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Europe | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87160 Polyvinyl Chloride, Rigid (PVC, Rigid)
- SABIC Innovative Plastics Lexan® FXG1414T PC Copolymer (Europe-Africa-Middle East)
- KaMin Hydrafine® 90W Clay
- LATI Latiohm 73-09 PD01 G/20 POM, 20% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC
- Engineered Syntactic Systems MZ-24 Deep Water Syntactic Foam
- A. Schulman POLYFORT™ FXP 1227U UV Stable Copolymer Polypropylene
- Epoxy Technology EPO-TEK® M10-D Epoxy Paste
- Chosun Refractories CSN-309NM,Insert Plate Brick
Copyright © lookpolymers.com All Rights Reserved