Arkema Group LOTADER® 8200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride

Category	Polymer , Thermoplastic , EMAAA Terpolymer
Manufacturer	Arkema
Trade Name	LOTADER®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group LOTADER® 8200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LOTADER 8200 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized under high pressure in an autoclave process. Due to its properties (reactivity, fluidity), LOTADER 8200 is an additive of choice for hot melt adhesives formulation. LOTADER 8200 can also be used as a modifier (processing aid) for rubbers of high hardness.Information provided by Arkema Group

Physical Properties	Metric	English	Comments
Density	0.940 g/cc @Temperature 23.0 °C	0.0340 lb/in³ @Temperature 73.4 °F	ISO 1183
Melt Index of Compound	200 g/10 min @Load 2.16 kg, Temperature 190 °C	200 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	26	26	ASTM D2240
Tensile Strength at Break	8.00 MPa	1160 psi	ASTM D638
Elongation at Break	400 %	400 %	ASTM D638
Flexural Modulus	0.0400 GPa	5.80 ksi	ASTM D638

Thermal Properties	Metric	English	Comments
Melting Point	100 °C	212 °F	DSC
Vicat Softening Point	61.0 °C @Load 0.999 kg	142 °F @Load 2.20 lb	ASTM D1525
Ring & Ball Softening Point	112 °C	234 °F	ASTM E28

Chemical Properties	Metric	English	Comments
Acid Value	17	17	mg KOH/g; Titration

Processing Properties	Metric	English	Comments
Processing Temperature	<= 300 °C	<= 572 °F

Descriptive Properties	Value	Comments
Ethyl Acrylate Content (%)	6.5	IRTF (internal)
Maleic Anhydride Content (%)	2.8	IRTF (internal)