Solvay TECHNYL® A 218 PA66, 33% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218 PA66, 33% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard viscosity, heat stabilized for injection molding. It is available in natural and black colors.Benefits: This product offers all the primary properties of unreinforced polyamide 66. In addition, it has improved resistance to high temperature, and can be used for components which will withstand long-term temperature stresses.Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Water Absorption | 1.3 % @Temperature 23.0 °C, Time 86400 sec |
1.3 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Viscosity | 20 cP @Shear Rate 1000 1/s, Temperature 290 °C |
20 cP @Shear Rate 1000 1/s, Temperature 554 °F |
shear rate: 1000/s |
| 20.5 cP @Shear Rate 1000 1/s, Temperature 280 °C |
20.5 cP @Shear Rate 1000 1/s, Temperature 536 °F |
shear rate: 1000/s | |
| 60 cP @Shear Rate 100 1/s, Temperature 300 °C |
60 cP @Shear Rate 100 1/s, Temperature 572 °F |
shear rate: 100/s | |
| 70 cP @Shear Rate 100 1/s, Temperature 290 °C |
70 cP @Shear Rate 100 1/s, Temperature 554 °F |
shear rate: 100/s | |
| 100 cP @Shear Rate 100 1/s, Temperature 280 °C |
100 cP @Shear Rate 100 1/s, Temperature 536 °F |
shear rate: 100/s | |
| 101 cP @Shear Rate 10.0 1/s, Temperature 300 °C |
101 cP @Shear Rate 10.0 1/s, Temperature 572 °F |
shear rate: 10/s | |
| 105 cP @Shear Rate 10.0 1/s, Temperature 290 °C |
105 cP @Shear Rate 10.0 1/s, Temperature 554 °F |
shear rate: 10/s | |
| 120 cP @Shear Rate 10.0 1/s, Temperature 280 °C |
120 cP @Shear Rate 10.0 1/s, Temperature 536 °F |
shear rate: 10/s | |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527 Type 1A |
| Tensile Stress | 30.0 MPa @Strain 1.00 % |
4350 psi @Strain 1.00 % |
|
| 58.0 MPa @Strain 2.00 % |
8410 psi @Strain 2.00 % |
||
| 78.0 MPa @Strain 3.00 % |
11300 psi @Strain 3.00 % |
||
| 85.0 MPa @Strain 4.00 % |
12300 psi @Strain 4.00 % |
||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ISO 527 type 1 A |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| 50 % | 50 % | ISO 527 Type 1A | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 type 1 A |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 Type 1A |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| 125 MPa | 18100 psi | ASTM D790 | |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| 3.30 GPa | 479 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75/Af |
| 220 °C | 428 °F | ASTM D648 | |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
1210 |
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
1210 | |
| Oxygen Index | 26 % | 26 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 2.9 | 2.9 | IEC 60250 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243 |
| Dissipation Factor | 0.030 | 0.030 | IEC 60250 |
| Comparative Tracking Index | 350 V | 350 V | Solution B; IEC 60112 |
| 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 265 - 275 °C | 509 - 527 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C | |
| Mixing Zone | 280-290°C |
Users viewing this material also viewed the following:
- LG Chemical LUPOL GP3300 PP+MF30%
- Gromax BFG15-DN00N1 Nylon 6 16% Glass Filled (Conditioned)
- Total MDPE 3802 B Medium Density Polyethylene, Pipes & Fittings
- A. Schulman POLYBATCH™ Mahogany 50381 Concentrate Based in Polyethylene
- A. Schulman POLYFORT™ FXP 2600-3120 CaC02 Filled Homopolymer Polypropylene
- Buckeye Polymers BP Flex A9008 TPO
Copyright © lookpolymers.com All Rights Reserved