SABIC Innovative Plastics Valox® SHF4960 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® SHF4960 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Valox Super high flow grade, 30% glass filled Flame retardant, High CTI, heat stabilized with mold release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ASTM D792 |
| Density | 1.69 g/cc | 0.0611 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ASTM D229 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.25 % | 0.25 % | ISO 62 |
| Viscosity | 68000 cP | 68000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| 110000 cP | 110000 cP | Melt Viscosity, 250°C, 1500 sec-1; ISO 11443 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | on Tensile Bar; SABIC Method |
| 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| 9.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 | |
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 50 g/10 min @Load 5.00 kg, Temperature 250 °C |
50 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ISO 2039-2 |
| Hardness, H358/30 | 220 MPa | 31900 psi | ISO 2039-1 |
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| 125 MPa | 18100 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| 125 MPa | 18100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| 2.0 % | 2.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 5 mm/min; ASTM D638 |
| 11.0 GPa | 1600 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 185 MPa | 26800 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 177 MPa | 25700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 185 MPa | 26800 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 9.45 GPa | 1370 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.60 GPa | 1390 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 0.800 J/cm @Temperature 0.000 °C |
1.50 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.800 J/cm @Temperature -30.0 °C |
1.50 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 5.90 J/cm | 11.1 ft-lb/in | ASTM D4812 |
| 5.80 J/cm @Temperature -30.0 °C |
10.9 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| 9.00 kJ/m² @Temperature 0.000 °C |
4.28 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| 40.0 kJ/m² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/2C |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/2C | |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Dart Drop, Total Energy | 60.0 J @Temperature 23.0 °C |
44.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 25.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 86.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | ASTM D257 |
| 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 | |
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | ROA; IEC 60093 |
| Dielectric Strength | 17.8 kV/mm @Thickness 3.20 mm |
452 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 24.5 kV/mm @Thickness 1.50 mm |
622 kV/in @Thickness 0.0591 in |
in oil; IEC 60243-1 | |
| 24.5 kV/mm @Thickness 1.60 mm |
622 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 35.0 kV/mm @Thickness 0.800 mm |
889 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.017 @Frequency 1.00e+6 Hz |
0.017 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 275 V | 275 V | IEC 60112 |
| 250 - 400 V | 250 - 400 V | UL 746A | |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
Users viewing this material also viewed the following:
- Polimeri Europa SINKRAL C350 ABS, Heat Stabilized (discontinued **)
- Westlake EB561 6.5% Ethylene Vinyl Acetate Copolymer (discontinued **)
- Lucent Polymers PBT-310 Polybutylene Terephthalate, 30% Glass Fiber/Mineral Reinforced, Low Warp
- Trelleborg AEM Eccospheres® SI-350 Sodium Borosilicate Glass Microspheres
- DSM Akulon® Ultraflow™ K-FHG0 Nylon 6-50% Glass Reinforced (European Grade) (Cond)
- Eurotec® Tecodur® PB70 GR15 NL XA 20 PBT 15% glass fiber reinforced, UL94 V0
- CLAL-MSX ARCAP Anticorrosion AP1D H14 4/4 hard, Drawn Copper Alloy, Wire and rod, 2.5< diameter< 5
- 3M XT2105 Hi-Tack Adhesive Transfer Tape
Copyright © lookpolymers.com All Rights Reserved