SABIC Innovative Plastics LNP STAT-KON DE0029 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE0029 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DE0029 is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0019 cm/cm @Time 86400 sec |
0.0019 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0039 cm/cm @Time 86400 sec |
0.0039 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 104 MPa | 15100 psi | ASTM D638 |
| 104 MPa | 15100 psi | ISO 527 | |
| Elongation at Break | 5.9 % | 5.9 % | ASTM D638 |
| 6.2 % | 6.2 % | ISO 527 | |
| Flexural Strength | 149 MPa | 21600 psi | ISO 178 |
| 158 MPa | 22900 psi | ASTM D790 | |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ISO 178 |
| 7.58 GPa | 1100 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.90 J/cm | 9.18 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 - 1.00e+7 ohm-cm | 10000 - 1.00e+7 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Raschig Group MELOPAS® 6605 MP Melamine
- Parker Chomerics CHO-SHIELD® 2054 Conductive Coating
- Schott N-SF8 Glass
- Shuman SP980 Grey Polycarbonate
- Teknor Apex Telcar® TL-2590A Thermoplastic Elastomer
- Trelleborg Emerson & Cuming Stycast® 1265 Two-Component Easy Mix Ratio Encapsulant
- DSM Stanyl® TW241F3 Nylon 46-15% Glass Reinforced, Heat Stabilized, Lubricated (Asian Grade) (Dry)
- 3M Scotchcast™ 265 Electrical Epoxy Powder Resin
- 3M Scotch-Weld™ Foam Fast 74 Cylinder Spray Adhesive
- 3M Novec™ Contact Cleaner Plus
Copyright © lookpolymers.com All Rights Reserved