SABIC Innovative Plastics NORYL V02570 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL V02570 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating at 1.0 mm. Noryl V02570 is may be an excellent material candidate for application requiring electrically insulating properties, low warpage and thin wall flame resistance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.25 % | 0.25 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | on Tensile Bar; SABIC Method |
| 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method | |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 300 °C |
12 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 8.0 g/10 min @Load 5.00 kg, Temperature 300 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 115 MPa | 16700 psi | ISO 2039-1 |
| Tensile Strength at Break | 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 |
| 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 |
| 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.60 GPa | 522 ksi | 5 mm/min; ASTM D638 |
| 4.70 GPa | 682 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 115 MPa | 16700 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 123 MPa | 17800 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.80 GPa | 551 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.80 GPa | 551 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 |
| 0.350 J/cm @Temperature -30.0 °C |
0.656 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | <= 155 °C | <= 311 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 160 °C | 320 °F | Rate B/50; ISO 306 |
| 165 °C | 329 °F | Rate B/50; ASTM D1525 | |
| 167 °C | 333 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.00 mm |
V-0 @Thickness 0.0394 in |
UL 94 |
| Oxygen Index | 32 % | 32 % | ISO 4589 |
| Glow Wire Test | 775 °C | 1430 °F | IEC 60695-2-13 |
| 775 °C | 1430 °F | IEC 60695-2-13 | |
| 825 °C | 1520 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.0 @Frequency 50.0 - 60.0 Hz |
3.0 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 18.0 kV/mm @Thickness 3.20 mm |
457 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 26.0 kV/mm @Thickness 1.60 mm |
660 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 33.0 kV/mm @Thickness 0.800 mm |
838 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0040 @Frequency 1.00e+6 Hz |
0.0040 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.0050 @Frequency 50.0 - 60.0 Hz |
0.0050 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| High Voltage Arc Resistance to Ignition (HVAR) | 0.00 - 30 sec | 0.00 - 30 sec | UL 746A |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Multibase TPSiV™ 3340-55A Thermoplastic Silicone Vulcanizate
- Plastcom SLOVAMID 6 GF 30 LS Polyamide 6, 30% Glass Fiber, UV Stabilization
- Solvay Specialty Polymers Ixef® 1521 Polyarylamide (PARA) (Unverified Data**)
- Styrolution Luran® S 767KE ASA
- SK Chemicals SKYTHANE® U0351C Ink Binder
- A. Schulman PP 3476 Polypropylene Homopolymer Polypropylene
- Covestro Bayfill® EA 6003 Polyurethane Energy-Absorbing Semi-Rigid Foam, Recoverable Grade, MDI-based 2-Component Liquid System
- Axiall 2134N Moldings & Extrusions Flexible PVC
- BNZ Materials 460 Insulating Cement
Copyright © lookpolymers.com All Rights Reserved