SABIC Innovative Plastics NORYL PPX PPX7110 PPE+PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl PPX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PPX PPX7110 PPE+PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPX7110 is an alloy of PP and PPO, providing high impact and good heat resistance. Generic identification acc. ISO11469: >PP+PPE+PS-I
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ISO 1183 |
| Melt Index of Compound | 11 g/10 min @Load 5.00 kg, Temperature 260 °C |
11 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 65.0 MPa | 9430 psi | ISO 2039-1 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 195 % | 195 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 1.50 GPa | 218 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 50.0 MPa | 7250 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.80 J/cm² @Temperature -30.0 °C |
18.1 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 75 | 75 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature 23.0 - 60.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 95.0 °C | 203 °F | Rate B/50; ISO 306 |
| 100 °C | 212 °F | Rate B/120; ISO 306 | |
| Glow Wire Test | 650 °C @Thickness 3.20 mm |
1200 °F @Thickness 0.126 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.2 @Frequency 1.00e+6 Hz |
2.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.2 @Frequency 50.0 - 60.0 Hz |
2.2 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 22.0 kV/mm @Thickness 3.20 mm |
559 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.00060 @Frequency 50.0 - 60.0 Hz |
0.00060 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.00060 @Frequency 1.00e+6 Hz |
0.00060 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
Users viewing this material also viewed the following:
- Reliance Industries Repol H110MA Polypropylene
- Michelman® Licomer® A 53 Acrylic polymer dispersion
- Kraton® D1133 K (SBS) Linear Block Copolymer
- Taiwan Sheen Soon Sheenthane® A8760 Thermoplastic Polyurethane Elastomer
- SABIC Innovative Plastics LNP LUBRILOY UA200A PPA (Asia Pacific)
- SABIC Innovative Plastics ULTEM HU2210 PEI
- Saint-Gobain CHR® M835 Polyester Film Backing Silicone Adhesive Pressure Sensitive Tape
- Carpenter Custom 450® Stainless Steel, Condition H1000 (Age Hardened 538°C (1000°F))
- Ashley Polymers Ashlene® 630-33G Nylon 6, 33% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved