Polymer Property : Flexural Modulus = 247 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	1.70 GPa	247 ksi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Nima™ NH PA66UT Nylon 66 Polyamide 66 - Ultra Tough, Flame Retarded Non-Hal grade with excellent retention of mechanical properties. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humi..
Flexural Modulus	1.70 - 2.20 GPa	247 - 319 ksi
Prodways PLASTCure Clear 100 3D Printing Polymer Ultra clear.Meet criteria regarding irritation, sensitisation and cytotoxicity for biological assessment of medical products (DIN ISO 10993)Wide range of medical applicationInformation provided by G..
Flexural Modulus	1.70 - 2.20 GPa	247 - 319 ksi
Prodways PLASTCure Model 100 3D Printing Polymer Allows production of precise components; high workability.Used for dental applications from models for restorations to orthodontics.Information provided by Genistar.
Flexural Modulus	1.70 - 2.20 GPa	247 - 319 ksi	ASTM D790-04
Proto3000 Objet Digital Materials™ RGD5160-DM ABS-like Prototyping Polymer Objet ABS-like Digital Material made of Object RGD515 & Objet RGD535Digital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to..
Flexural Modulus	1.70 GPa @Temperature 23.0 °C	247 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYfill PPC GK8020 Polypropylene Copolymer, Glass Fiber Reinforced Information provided by Polykemi AB
Flexural Modulus	1.70 GPa @Temperature 23.0 °C	247 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYfill PPC TS15020E Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
Nilit FRIANYL C73 HS28 Nylon 6.6/6 for injection molding Nylon 6.6/6 for injection molding, medium viscosity, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
Grupo Repol DinalonÂ® A3S25 PA66 Unreinforced Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
Flexural Modulus	1.70 GPa	247 ksi	ASTM D790
Ineos ABS TriaxÂ® 1220 S ABS + Polyamide Blend, Extrusion, Conditioned Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
Flexural Modulus	1.70 GPa	247 ksi
Spartech Royalstatâ„¢ R671 ABS Static Control Sheet Data provided by the manufacturer.
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP MB006S PP (Europe-Africa-Middle East) LNP* Thermocomp* MB006S is a compound based on Polypropylene resin containing Glass Bead. Added features of this material include: Heat Stabilized.
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics XYLEX X8300 PC+POLYESTER (Europe-Africa-Middle East) PC+Polyester, UV Stabilized, Transparent
Flexural Modulus	1.70 GPa	247 ksi	At 2 mm/min; ISO 178
Borealis BorECO™ BA212E Polypropylene Block Copolymer for Non-Pressure Pipes BorECO BA212E is a high molecular weight, low melt flow rate polypropylene block copolymer with very high stiffness and impact strength.BorECO BA212E is recommended for solid wall and structured wal..
Flexural Modulus	1.70 GPa	247 ksi	At 2 mm/min; ISO 178
Borealis Daplen™ EE137AI Polypropylene Compound 10% Mineral Filled Daplen EE137AI is a 10% mineral filled grade intended for injection molding. EE137AI has been developed especially for the car industry, to be used in interior parts where high scratch resistance i..
Flexural Modulus	1.70 GPa	247 ksi	2mm/min; ISO 178
Borealis Daplen™ EF210AE Polypropylene TPO Compound Daplen™ EF210AE is a 20% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, gives a good surface q..
Flexural Modulus	1.70 GPa	247 ksi	ASTM D790
Total PSI 8350 (AS) High Impact Polystyrene Total Petrochemicals Polystyrene 8350 (AS) is a very high impact polystyrene for extrusion and injection molding. This grade has improved environmental stress crack resistance in comparison with st..
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
Total PPC 1645 Polypropylene, Heterophasic Copolymer, Pipes Polypropylene PPC 1645 is a nucleated heterophasic (block) copolymer with a Melt Flow index of 0.3 g/10 min. This resin has a long-term heat stabilization package. It offers a very high stiffness ..
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
ExxonMobil Exxtral™ BMU 143S Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin characterized by a good stiffness/toughness balance and designed for automotive interior application in which good surface finish, hig..
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
Chi Mei Polylac® PA-747R ABS - Extrusion Attach case and refrigerator
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
Eurostar Starpylen MK001AS PP, Mineral Filled, Injection Molding Starpylen MK001AS is a Mineral Filled Polypropylene Injection Molding ResinInformation provided by Eurostar.
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
Eurostar Staramide Z1000XXC PA66, Injection Molded Staramide Z1000XXC is an UV Stabilized Polyamide 66 Injection Molding Resin (also known as R1000HI0944)Information provided by Eurostar.
Flexural Modulus	1.70 GPa	247 ksi	ASTM D790
A. Schulman ComAlloy Comtuf® 420 Polyester - PBT, High Impact Modified Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc..
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
Unitika ET2025 PA6, Dry High-impact nylonInformation provided by Unitika Ltd.
Flexural Modulus	1.70 GPa	247 ksi	ASTM D790
Adell RA-14 Copolymer Polypropylene, 20% Talc Filled Data provided by Adell Plastics, Inc.
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
SABIC Innovative Plastics LNP THERMOTUF V1000SU PA (Asia Pacific) LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized.
Flexural Modulus	1.70 GPa	247 ksi
Kraton® G1657 + PA-6 blend (16/4/80) Blending KRATON D and G polymers with PA significantly improves the toughness at both room and low temperatures. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A..
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
LyondellBasell Hostacom™ ZG750 Polypropylene Copolymer Description: Hostacom™ ZG750 conventional melt flow, 1,700 MPa flexural modulus, 40% calcium carbonate-filled, utility grade polypropylene copolymer resin has a very good combination of strength, s..