Polymer Property : Flexural Modulus = 1.70 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	1.70 GPa	247 ksi	STN EN ISO 178
Plastcom PLASTALEN® PH 52 T 20 003/1M Polypropylene reinforced with 20% mineral filler PP homopolymer for injection molding with the content of 20 % mineral filler, heat stabilized. Application in automotive industry. Delivered in black grade.Information Provided by Plastcom spol. s r..
Flexural Modulus	1.70 GPa	247 ksi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Nima™ NH PA66UT Nylon 66 Polyamide 66 - Ultra Tough, Flame Retarded Non-Hal grade with excellent retention of mechanical properties. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humi..
Flexural Modulus	1.70 GPa @Temperature 23.0 °C	247 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYelast TPE HJ752 Thermoplastic Elastomer, PP/Elastomer, Mineral Reinforced Information provided by Polykemi AB
Flexural Modulus	1.70 GPa @Temperature 23.0 °C	247 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYfill PPC TS15020E Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Modulus	1.70 - 2.70 GPa @Temperature 40.0 - 130 °C	247 - 392 ksi @Temperature 104 - 266 °F	Average value: 2.13 GPa Grade Count:2
Overview of materials for Cyclo Olefin Polymer This property data is a summary of similar materials in the MatWeb database for the category "Cyclo Olefin Polymer". Each property range of values reported is minimum and maximum values of appropria..
Flexural Modulus	1.70 GPa	247 ksi
KratonÂ® G1657 + PA-6 blend (8/12/80) Blending KRATON D and G polymers with PA significantly improves the toughness at both room and low temperatures. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A..
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
Grupo Repol DinalonÂ® A1S25 MI PA66 Medium Impact Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
Grupo Repol DinalonÂ® A3S25 PA66 Unreinforced Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
Flexural Modulus	1.70 GPa	247 ksi	Tangent at 0.05 in/min; ASTM D790A
LyondellBasell Astryn 68F4-2 Polypropylene Homopolymer, 20% Talc Key Features: fractional melt flow, medium high modulus, mineral-filled, blow molding and extrusion grade polypropylene homopolymer, excellent impact and stiffness balance, good processabilityApplic..
Flexural Modulus	1.70 GPa	247 ksi	1% Secant, 0.2 in/min; ASTM D790
LyondellBasell Hostacomâ„¢ BG722AC Polypropylene Copolymer Description: Hostacomâ„¢ BG722AC medium high melt flow, 1,700 MPa flexural modulus, precolored, mineral-filled polypropylene copolymer is designed with an excellent balance of stiffness, impact r..
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Lubricomp ML003 PP (Europe-Africa-Middle East) LNP* Lubricomp* ML003 is a compound based on Polypropylene resin containing PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Modulus	1.70 GPa	247 ksi
Spartech Royalstatâ„¢ R671 ABS Static Control Sheet Data provided by the manufacturer.
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Xylex X8300HP PC+POLYESTER (Asia Pacific) Transparent, US Food Contact compliant, chemically resistant. This grade will no longer be supported with biocompatibility information and should not be used for medical applications which require b..
Flexural Modulus	1.70 GPa	247 ksi	ASTM D790
Styrolution StyroluxÂ® 684 D SBC Description: StyroluxÂ® 684 D is a clear styrene-butadiene copolymer (SBC) used in injection molding for parts with enhanced toughness as well as in sheet and film extrusion and blow molding. Part..
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL PPX PPX7110 PPE+PP (Europe-Africa-Middle East) PPX7110 is an alloy of PP and PPO, providing high impact and good heat resistance. Generic identification acc. ISO11469: >PP+PPE+PS-I
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-LOY N30009 PC+ABS (Europe-Africa-Middle East) LNP* STATLOY* N30009 is a compound based on PC+ABS Blend resin containing Flame Retardant. Added features include: Permanent Antistatic, Flame Retardant.
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
SABIC Innovative Plastics LNP THERMOTUF V1000SU PA LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized.
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL ENV105 PPE+HIPS (Europe-Africa-Middle East) NORYL ENV105 is an impact modified extrusion grade with a Vicat B/120 of 115C according ISO 306.
Flexural Modulus	1.70 GPa	247 ksi	Tangent; ISO 178
A. Schulman FORMION™ FI 232H 10% Mineral Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 232H is an injection molding grade, 10% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, high stiffness and exceptional impact..
Flexural Modulus	1.70 GPa	247 ksi	2mm/min; ISO 178
Borealis Daplen™ EF210AE Polypropylene TPO Compound Daplen™ EF210AE is a 20% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, gives a good surface q..
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
Unipetrol PP MONSTEN® TB 002 Polypropylene Homopolymer Applications include injection molding, extrusion, tapes, and thermoforming. Basic stabilization. Homopolymer.Information provided by Unipetrol RPA
Flexural Modulus	1.70 GPa	247 ksi	Tangent; ISO 178
A. Schulman FORMION™ FI 232H 10% Mineral Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 232H is an injection molding grade, 10% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, high stiffness and exceptional impact..
Flexural Modulus	1.70 GPa	247 ksi	dry; ISO 178
DSM Novamid® ST120 NAT PA6-I Impact Modified, Injection Molding
Flexural Modulus	1.70 GPa	247 ksi	ASTM D790
Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, 50% RH Neat resin, for film or extrusion.Information provided by Cresset Powers Ltd.
Flexural Modulus	1.70 GPa	247 ksi	2 mm/min; ISO 178
Eurostar Staramide Z1000XXC PA66, Injection Molded Staramide Z1000XXC is an UV Stabilized Polyamide 66 Injection Molding Resin (also known as R1000HI0944)Information provided by Eurostar.
Flexural Modulus	1.70 GPa	247 ksi	ASTM D790
A. Schulman ComAlloy Comtuf® 109 Polypropylene, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i..
Flexural Modulus	1.70 GPa	247 ksi	ASTM D790
Beijing Chemical Industry KAIFA® 201-G0R PBT Resin Good flow and toughnessInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
SABIC Innovative Plastics LNP THERMOTUF V1000SU PA (Asia Pacific) LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized.
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
LyondellBasell Hostacom™ ZG750 Polypropylene Copolymer Description: Hostacom™ ZG750 conventional melt flow, 1,700 MPa flexural modulus, 40% calcium carbonate-filled, utility grade polypropylene copolymer resin has a very good combination of strength, s..