SABIC Innovative Plastics NORYL NH7114 PPE+HIPS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL NH7114 PPE+HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of strength and dimensional stability. This grade can be processed via extrusion or injection molding. Noryl NH7114 is available in custom colors and may be an excellent material candidate for use in electrical and electronics markets.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.22 % | 0.22 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 5.8 g/10 min @Load 5.00 kg, Temperature 280 °C |
5.8 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 300 °C |
10 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.80 GPa | 986 ksi | 5 mm/min; ASTM D638 |
| 6.80 GPa | 986 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
| 152 MPa | 22000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 6.00 GPa | 870 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.30 GPa | 914 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.770 J/cm | 1.44 ft-lb/in | ASTM D256 |
| 0.700 J/cm @Temperature -30.0 °C |
1.31 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| 27.0 kJ/m² @Temperature -30.0 °C |
12.8 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 51.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 51.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 148 °C | 298 °F | Rate B/50; ASTM D1525 |
| 148 °C | 298 °F | Rate B/50; ISO 306 | |
| 150 °C | 302 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
UL 94 by SABIC-IP | |
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
UL 94 by SABIC-IP | |
| Oxygen Index | 30 % | 30 % | ISO 4589 |
| Glow Wire Test | 800 °C | 1470 °F | IEC 60695-2-13 |
| 800 °C | 1470 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 5.00e+17 ohm | >= 5.00e+17 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.73 @Frequency 1.00e+6 Hz |
2.73 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm |
406 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 25.0 kV/mm @Thickness 3.20 mm |
635 kV/in @Thickness 0.126 in |
in oil; ASTM D149 | |
| Dissipation Factor | 0.0029 @Frequency 1.00e+6 Hz |
0.0029 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.0029 @Frequency 1.00e+6 Hz |
0.0029 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Arc Resistance | 180 - 240 sec | 180 - 240 sec | UL 746A |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Parker Chomerics THERM-A-FORM T644 Cure-in-Place Potting and Underfill Material
- BASF Capron® 8224 HSL Nylon 6 (DAM) (discontinued **)
- LATI Latilub 80-10T G/40 PPS, 40% Glass Fiber Reinforced, PTFE Filled
- Heraeus Cleviosâ„¢ PH 1000 Conductive Sulfonate Polymer for Antistatic Coatings
- Solvay Specialty Polymers Ixef® 1025 Polyarylamide (PARA), 50% Glass Fiber
- Borealis Himod™ FT7294 LDPE for Film
- Fainplast Compounds CRKA 91 Flexible PVC, Flame Retardant Electrical Bedding Lead Free
- BASF Lupranate® 5220 Isocyanate
- ConocoPhillips Hydroclear Diamond Class® 68 Turbine Oil
Copyright © lookpolymers.com All Rights Reserved