Ineos Nova Zyntar® 7000 Flame Retardant Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant |
| Manufacturer | Ineos Nova |
| Trade Name | Zyntar® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Nova Zyntar® 7000 Flame Retardant Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:General purpose workhorse resinGood flow for injection moldingUL94 V-0 @ 1.5 mm for all colors UL94 5VA rating FOAMED @ 4.6 mm, 0.87-1.07 g/cc density, natural colorCustom colors availableApplications:Television cabinets (front bezel, TV backs)Consumer electronicsExercise equipmentBusiness equipmentInformation provided by Nova Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets.Â
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 200 °C |
11 g/10 min @Load 11.0 lb, Temperature 392 °F |
Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 171 - 193 °C | 340 - 379 °F | |
| Middle Barrel Temperature | 199 - 221 °C | 390 - 430 °F | |
| Front Barrel Temperature | 210 - 232 °C | 410 - 450 °F | |
| Melt Temperature | 210 - 232 °C | 410 - 450 °F | |
| Mold Temperature | 32.0 - 54.0 °C | 89.6 - 129 °F | |
| Back Pressure | 0.345 MPa | 50.0 psi |
Users viewing this material also viewed the following:
- MV Labs ER300 Er2(CO3)3·xH2O Erbium carbonate hydrate
- Less Common Metals Praseodymium Vacuum Remelted Rare Earth Metal
- Industeel FORA 360 BC 360 HB Wear Resistant Steel
- Seals Eastern 7182A Fluorocarbon-Elastomer
- A. Schulman PP 3490-01G Polypropylene Homopolymer Polypropylene
- CP-Polymer-Technik Wellamid® 6600/50 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Dry
- SABIC Innovative Plastics LNP LUBRICOMP DFL329 PC
- BASF Pluracol® 1421 Molded Foam Polyol
Copyright © lookpolymers.com All Rights Reserved