Polymer Property : Tensile Strength at Break = 107 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	107 MPa	15500 psi	ASTM D638
Niche Polymer PA66GF13BK Nylon 66, 13% Glass Fiber Filled Information provided by Niche Polymer
Tensile Strength at Break	107 MPa	15500 psi	ASTM D638
Niche Polymer PA66GF13N Nylon 66, 13% Glass Fiber Filled Information provided by Niche Polymer
Tensile Strength at Break	107 MPa	15500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics EXTEM UH1006 TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical Resistant
Tensile Strength at Break	107 MPa	15500 psi	ASTM D638
Polymer Resources PC-G20-[color]-WS Polycarbonate, 20% Glass Reinforced Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Tensile Strength at Break	107 MPa	15500 psi	ASTM D638
Polymer Resources TP-IGFR-G30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant, Reduced Warpage Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant, Reduced WarpageProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmen..
Tensile Strength at Break	107 MPa	15500 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne Edgetek® PC-20GF/000 Polycarbonate (PC) Information provided by PolyOne
Tensile Strength at Break	107 MPa	15500 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Lubricomp EFP36G PEI LNP* EFP36G is a Polyetherimide base resin containing a Mixed Glass Fiber and PTFE/Silicone.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	107 MPa	15500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RFL32 PA 66 LNP* Lubricomp* RFL32 is a compound based on Nylon 66 containing 10% Glass Fiber, 15% PTFE. Added feature of this material includes: Wear Resistant.
Tensile Strength at Break	107 MPa	15500 psi	ISO 527
SABIC Innovative Plastics LNP STAT-KON DX05474 PC LNP* STAT-KON* DX05474 is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Retardant, Mold ..
Tensile Strength at Break	107 MPa	15500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® K4560 PBT 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable.
Tensile Strength at Break	107 MPa	15500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® K4560 PBT (Europe-Africa-Middle East) 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable.
Tensile Strength at Break	107 MPa	15500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF005 PC LNP* Thermocomp* DF005 is a compound based on Polycarbonate containing 25% Glass Fiber.
Tensile Strength at Break	107 MPa	15500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF003E PES LNP* THERMOCOMP* JF003E is a compound based on Polyethersulfone resin containing 15% Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break	107 MPa	15500 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGN2000 PC (Asia Pacific)
Tensile Strength at Break	107 MPa	15500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOTUF RF002I PA 66 (Asia Pacific) LNP* THERMOTUF* RF002I is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact.
Tensile Strength at Break	107 MPa	15500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP VERTON MV00ES PP LNP* VERTON* MV00ES is primarily a concentrate used for blending purposes. This is a 70% long glass fiber Polypropylene compound. Added features of this grade are: Heat Stabilized
Tensile Strength at Break	107 MPa	15500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Asia Pacific) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng..
Tensile Strength at Break	107 MPa	15500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng..
Tensile Strength at Break	107 MPa	15500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Noryl_HM3020 PPE+HIPS (Europe-Africa-Middle East) LNP* Thermocomp* Noryl_HM3020 compound is a 30% Glass/Mineral filled, high modulus grade. DTUL 248F (120C). UL94 V-1/5VA rated in black and gray.
Tensile Strength at Break	107 MPa	15500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PX92248 PA 6 LNP* THERMOCOMP* PX92248 is a compound based on Nylon 6 resin containing Proprietary Filler(s).
Tensile Strength at Break	107 MPa	15500 psi	ASTM D638
Chase Plastics CP Pryme® PC120R Polycarbonate, 20% Glass Fiber Reinforced Features: Good mold releaseForm: PelletsInformation provided by Chase Plastics.
Tensile Strength at Break	107 MPa	15500 psi	ISO 527-1/-2
DuPont Performance Polymers Rynite® FR515 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**) 15% Glass Reinforced Flame Retardant Polyethylene Terephthalate Rynite FR515 NC010 is a flame retardant 15% glass reinforced modified polyethylene terephthalate. Recognized by UL as UL94V-0 at 0.8mm..