SABIC Innovative Plastics NORYL NH6020 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL NH6020 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl NH6020 resin is an unfilled, injection moldable modified polyphenylene ether resin. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 0.8 mm and is also non-halogenated according to VDE/DIN 472 part 815. Noryl NH6020 resin has a HDT > of 120 deg C, pass the BPT @ 125 deg C, pass the GWIT 775 deg C @ 1, 2 and 3 mm, has the CTI value > 250 V and may be an excellent material candidate for unattended appliances components, where IEC 60335 applies.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.18 % | 0.18 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 13.5 g/10 min @Load 5.00 kg, Temperature 280 °C |
13.5 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 11 g/10 min @Load 5.00 kg, Temperature 280 °C |
11 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
| 67.0 MPa | 9720 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 77.0 MPa | 11200 psi | 50 mm/min; ISO 527 |
| 78.0 MPa | 11300 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 4.2 % | 4.2 % | 50 mm/min; ISO 527 |
| 6.1 % | 6.1 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.6 % | 4.6 % | Type I, 50 mm/min; ASTM D638 |
| 4.6 % | 4.6 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.74 GPa | 397 ksi | 5 mm/min; ASTM D638 |
| 2.74 GPa | 397 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 114 MPa | 16500 psi | 2 mm/min; ISO 178 |
| 121 MPa | 17500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.68 GPa | 389 ksi | 2 mm/min; ISO 178 |
| 3.02 GPa | 438 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| 0.360 J/cm @Temperature -30.0 °C |
0.674 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 18.0 J @Temperature 23.0 °C |
13.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 77.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 77.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60695-10-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 141 °C | 286 °F | Rate B/50; ISO 306 |
| 150 °C | 302 °F | Rate B/50; ASTM D1525 | |
| 151 °C | 304 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 by SABIC-IP |
| 5VB @Thickness 2.50 mm |
5VB @Thickness 0.0984 in |
UL 94 by SABIC-IP | |
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
UL 94 by SABIC-IP | |
| Glow Wire Test | 800 °C | 1470 °F | IEC 60695-2-13 |
| 800 °C | 1470 °F | IEC 60695-2-13 | |
| 825 °C | 1520 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.50e+16 - 4.15e+16 ohm-cm | 2.50e+16 - 4.15e+16 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.7 @Frequency 50.0 - 60.0 Hz |
2.7 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| Dielectric Strength | 27.0 kV/mm @Thickness 1.60 mm |
686 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0029 @Frequency 1.00e+6 Hz |
0.0029 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 30 FRG 5 Polyamide 6, 30% Glass Fiber, Halogen Free Flame Retardant
- Nye Lubricants UniFlor 8521R (841RP-1) (UF) Synthetic Oil
- Network Polymers Kepital® TC30-20
- Solvay Engineered Polymers SEQUEL® 2322 Engineered Polyolefin (discontinued **)
- ICO Polymers ICORENEâ„¢ 195-4060 LMDPE Rotational Molding Resin
- Silon Taborex TA 2126 HD Catalyst Masterbatch
- Chosun Refractories A70 Special High-Density Gunning Castable
- Dymax Sure Cure™ 984 Conformal Coating
- 3M Dyneon™ PVDF 31508/0001 Polyvinylidene Fluoride (discontinued **)
Copyright © lookpolymers.com All Rights Reserved