- SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Asia Pacific)
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity. This grade can be processed via extrusion or injection molding. Noryl NH6010B is available in custom colors and may be an excellent material candidate for use in building and construction and electrical markets.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 5.6 g/10 min @Load 5.00 kg, Temperature 280 °C |
5.6 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 5.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | 4min; ISO 5659-2 |
| Tensile Strength at Break | 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 |
| 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
| 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 8.3 % | 8.3 % | 50 mm/min; ISO 527 |
| 20 % | 20 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.6 % | 4.6 % | Type I, 50 mm/min; ASTM D638 |
| 4.7 % | 4.7 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.22 GPa | 322 ksi | 5 mm/min; ASTM D638 |
| 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 100 MPa | 14500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 100 MPa | 14500 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| 2.39 GPa | 347 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 3.00 J/cm | 5.62 ft-lb/in | ASTM D256 |
| 1.81 J/cm @Temperature -30.0 °C |
3.39 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| 14.0 kJ/m² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 52.0 J @Temperature 23.0 °C |
38.4 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 67.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 67.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 67.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 143 °C | 289 °F | Rate B/50; ASTM D1525 |
| 143 °C | 289 °F | Rate B/50; ISO 306 | |
| 146 °C | 295 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Oxygen Index | 33 % | 33 % | ISO 4589 |
| Glow Wire Test | 775 °C | 1430 °F | IEC 60695-2-13 |
| 775 °C | 1430 °F | IEC 60695-2-13 | |
| 800 °C | 1470 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 1.50 mm |
1760 °F @Thickness 0.0591 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.62e+17 ohm-cm | 7.62e+17 ohm-cm | ASTM D257 |
| 7.62e+17 ohm-cm | 7.62e+17 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.25e+18 ohm | 1.25e+18 ohm | ASTM D257 |
| 1.25e+18 ohm | 1.25e+18 ohm | ROA; IEC 60093 | |
| Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.78 @Frequency 1.00e+6 Hz |
2.78 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 34.1 kV/mm @Thickness 3.20 mm |
866 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| 34.1 kV/mm @Thickness 3.20 mm |
866 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0029 @Frequency 1.00e+6 Hz |
0.0029 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.0029 @Frequency 1.00e+6 Hz |
0.0029 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| F1 Class Smoke and Toxicity Rating | 3mm | NF F16-101 |
| Flame Spread Index (1.52mm) | 15 | ASTM E 162 |
| Heat Release, MAHRE | 33.6kW/m^2 | ISO 5660-1 |
| Lateral Flame Spread, CFE | 20kW/m^2 | ISO 5658-2 |
| M1 Flame Class Rating | 2mm | NF P 92501 |
| NBS Smoke Density, Flaming, 20 min (3.2 mm) | 120 | ASTM E 662 |
| NBS Smoke Density, Flaming, 4 min (1.52mm) | 30 | ASTM E 662 |
| NBS Smoke Density, Flaming, 4 min (3.2 mm) | 30 | ASTM E 662 |
| NBS Smoke Density, Non-Flaming, 4 min (1.52mm) | 7 | ASTM E 662 |
| Toxicity | 0 | ISO 5659-2 |
| Toxicity (3 mm) | 21.76 | NF X70-100 |
Users viewing this material also viewed the following:
- Multibase SILASTIC® Q7-4850 Dow-Corning Biomedical Grade Liquid Silicone Rubber
- SABIC Innovative Plastics Cycoloy® XCY630 PC+ABS (Europe-Africa-Middle East)
- Nilit FRIANYL B63 W-GV35 Nylon 6 for injection molding, 35% glass fiber reinforced
- SABIC Innovative Plastics Lexan® BFL2000B PC (Asia Pacific)
- Techmer ES HiFill® PA6 GF/M40 L 40% Glass/Mineral Filled
- SABIC Innovative Plastics Valox® IQ3001 PBT
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N339 Filler
- Arlon 910-05RXX-P0 0.010" (0.254 mm) Self-Fusing Silicone Tape
- Axiall 02541 Plenum Flexible PVC
Copyright © lookpolymers.com All Rights Reserved