SABIC Innovative Plastics NORYL N850 PPE+PS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL N850 PPE+PS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ECO-FLO(tm). ECO conforming, nonhalogenated flame retardant PPE+PS. High flow. Electrical and Business Equipment applications.
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 14 g/10 min

@Load 2.16 kg,
Temperature 220 °C
 14 g/10 min

@Load 4.76 lb,
Temperature 428 °F
 ASTM D1238
18 g/10 min

@Load 3.80 kg,
Temperature 260 °C
 18 g/10 min

@Load 8.38 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
Type I, 50 mm/min; ASTM D638
61.0 MPa
8850 psi
50 mm/min; ISO 527
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
66.0 MPa
9570 psi
50 mm/min; ISO 527
Elongation at Break 4.5 %
4.5 %
50 mm/min; ISO 527
18 %
18 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 3.2 %
3.2 %
50 mm/min; ISO 527
3.6 %
3.6 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.62 GPa
380 ksi
50 mm/min; ASTM D638
2.95 GPa
428 ksi
1 mm/min; ISO 527
Flexural Yield Strength 96.0 MPa
13900 psi
1.3 mm/min, 50 mm span; ASTM D790
107 MPa
15500 psi
2 mm/min; ISO 178
Flexural Modulus 2.41 GPa
350 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.60 GPa
377 ksi
2 mm/min; ISO 178
Izod Impact, Notched 2.13 J/cm
3.99 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
Dart Drop, Total Energy 31.0 J

@Temperature 23.0 °C
 22.9 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 77.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 43.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 81.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 45.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
93.0 °C

@Thickness 3.20 mm
 199 °F

@Thickness 0.126 in
 unannealed; ASTM D648
98.0 °C

@Thickness 6.40 mm
 208 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.0 °C
180 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
82.0 °C

@Thickness 3.20 mm
 180 °F

@Thickness 0.126 in
 unannealed; ASTM D648
86.0 °C

@Thickness 6.40 mm
 187 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 101 °C
214 °F
Rate B/50; ASTM D1525
108 °C
226 °F
Rate B/120; ISO 306
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 HB

@Thickness 0.990 mm
 HB

@Thickness 0.0390 in
 UL 94
V-0

@Thickness 1.49 mm
 V-0

@Thickness 0.0587 in
 UL 94
5VA

@Thickness 2.99 mm
 5VA

@Thickness 0.118 in
 UL 94
Oxygen Index 36.4 %
36.4 %
ASTM D2863
Electrical Properties Metric English Comments
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 30 - 60 arcs
30 - 60 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A
Descriptive Properties Value Comments
UV-light, water exposure/immersion F2
UL 746C