SABIC Innovative Plastics NORYL N300X PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL N300X PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.060 % | 0.060 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 7.4 g/10 min @Load 5.00 kg, Temperature 280 °C |
7.4 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 66.0 MPa | 9570 psi | ISO 527 |
| 73.0 MPa | 10600 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 50 mm/min; ASTM D638 |
| 75.0 MPa | 10900 psi | ISO 527 | |
| Elongation at Break | 7.6 % | 7.6 % | Type I, 50 mm/min; ASTM D638 |
| 13 % | 13 % | ISO 527 | |
| Elongation at Yield | 5.2 % | 5.2 % | ISO 527 |
| 5.3 % | 5.3 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.22 GPa | 322 ksi | 1 mm/min; ISO 527 |
| 2.38 GPa | 345 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 112 MPa | 16200 psi | ISO 178 |
| Flexural Yield Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 110 MPa | 16000 psi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 2.52 GPa | 365 ksi | ISO 178 | |
| 2.65 GPa | 384 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.90 J/cm | 3.56 ft-lb/in | ASTM D256 |
| 0.550 J/cm @Temperature -30.0 °C |
1.03 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 54.0 J @Temperature 23.0 °C |
39.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 155 °C @Thickness 3.20 mm |
311 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 145 °C @Thickness 6.40 mm |
293 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 162 °C | 324 °F | Rate B/50; ISO 306 |
| 164 °C | 327 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | ASTM D257 |
| Dielectric Constant | 2.63 @Frequency 1.00e+6 Hz |
2.63 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 2.68 @Frequency 50.0 - 60.0 Hz |
2.68 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 19.4 kV/mm @Thickness 3.20 mm |
493 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0031 @Frequency 50.0 - 60.0 Hz |
0.0031 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- MV Labs AL500 AlF3 Aluminum fluoride, anhydrous
- DSM Akulon® K-FHG12 (Cond.) 60% Glass Reinforced Nylon 6 (North America) (discontinued **)
- Ravago Manufacturing Americas Hylon® N1000STL Nylon 6/6 (DAM) (discontinued **)
- LyondellBasell Plexar® PX5125 Extrudable Tie-Layer Resin - Anhydride Modified LLDPE
- Kolon KOPA® KN333G35CR G/F Reinforced Nylon 66
- Glastic 4610-10-E Fiberglass-Reinforced Polyester Standoff Insulator
- Ferro EG 2805 Low-Temperature Sealing
- Ineos R01A-01 Polypropylene Copolymer, Antistatic
- Dow Corning XIAMETER® PMCPPMX-200 100,000CS Silicone Fluid
- Bhansali Engineering Abstron IM-18 ABS Heat Resistant
Copyright © lookpolymers.com All Rights Reserved