Polymer Property : Tensile Strength, Yield = 10700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	74.0 MPa	10700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Cycolac® INP563 ABS SABIC INP563 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet..
Tensile Strength, Yield	74.0 MPa	10700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Cycolac® INP563 ABS+SAN SABIC INP563 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet..
Tensile Strength, Yield	74.0 MPa	10700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FST9705 PC Copolymer High viscosity Proprietary Polycarbonate Ester, OSU 55/55 compliant, low smoke, flame retardant resin
Tensile Strength, Yield	74.0 MPa	10700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FST9705 PC Copolymer (Asia Pacific) High visocisty PC Copolymer, OSU 55/55 compliant, low smoke, flame retardant resin
Tensile Strength, Yield	74.0 MPa	10700 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL32 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL32 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE.
Tensile Strength, Yield	74.0 MPa	10700 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL12 PC LNP* Lubricomp* DFL12 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated.
Tensile Strength, Yield	73.5 - 165 MPa	10700 - 24000 psi	Average value: 133 MPa Grade Count:8
Overview of materials for Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled". Each property range of values reported is mini..
Tensile Strength, Yield	73.5 MPa	10700 psi	ASTM D638
Lendell Parapet EH-1000 PMMA, Extrusion
Tensile Strength, Yield	73.5 MPa @Thickness 3.20 mm	10700 psi @Thickness 0.126 in	5mm/min; ASTM D638
LG Chemical LUCON CP510F PC/ABS+CNT Description Injection Molding Grade, PC/ABS+CNT, Electrostatic Dissipation, High Flow, Good ProcessabilityApplication: Copy Machine Paper GuideCAS No. 103598-77-2 and 7440-44-0Information provided b..
Tensile Strength, Yield	73.5 MPa @Thickness 3.20 mm	10700 psi @Thickness 0.126 in	50mm/min; ASTM D638
LG Chemical 80HFICELLHK SAN, High Transparency, Heat Resistance, Chemical Resistance Feature: Injection Molding, SAN, High Transparency, Heat Resistance, Chemical ResistanceApplication: Refrigerator Sleeves, MiscellaneousCAS No. 9003-54-7Information provided by LG Chemical
Tensile Strength, Yield	74.0 MPa	10700 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK (Asia Pacific) LNP* Lubricomp* LL004C is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated, Clean Compounding System.
Tensile Strength, Yield	74.0 MPa	10700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP Noryl_NF1520 PPE+HIPS (Europe-Africa-Middle East) LNP* Lubricomp* Noryl_NF1520 compound is a 20% glass reinforced, 15% PTFE. Wear resistant; 211F HDT @ 264 psi.
Tensile Strength, Yield	74.0 MPa	10700 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP UAL22S PPA LNP* LUBRICOMP* UAL22S is a compound based on Polyphthalamide resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant, Heat Stabilized.
Tensile Strength, Yield	74.0 MPa	10700 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP UX06002 PPA (Europe-Africa-Middle East) LNP* LUBRICOMP* UX06002 is a compound based on Polyphthalamide resin containing Aramide Fiber, PTFE. Added features include: Easy Molding, Internally Lubricated, Heat Stabilized.
Tensile Strength, Yield	74.0 MPa	10700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM DU242 PEI Enhanced low temperature impact, high flow Polyetherimide blend. ECO Conforming.
Tensile Strength, Yield	73.5 MPa	10700 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® VG-4910 ABS, Glass Filled FR Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	73.5 MPa	10700 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® VG-4910 ABS, Glass Filled FR Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	74.0 MPa	10700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL HS2000X PPE+PS PPE+PS blend. 17% Mineral reinforced. Non-brominated, non-chlorinated FR system. UL94 V0 and 5VA listing. UL746C f1. Radiant panel listing. Dielectric strength. Dimensional stability. Suitable for E..
Tensile Strength, Yield	74.0 MPa	10700 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL N300X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications.
Tensile Strength, Yield	74.0 MPa	10700 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Tensile Strength, Yield	74.0 MPa	10700 psi	50 mm/min; ISO 527-1,-2
Covestro Apec® FR1892 High-Heat Polycarbonate This linear, amorphous copolycarbonate is most suitable for applications that must withstand high temperatures and exhibit toughness, impact resistance and high transparency. These properties, along..
Tensile Strength, Yield	74.0 MPa	10700 psi	ISO 527-1/-2
DuPont Performance Polymers Delrin® 511DP NC010 Acetal (POM)  (Unverified Data**) Nucleated Medium Viscosity Acetal Homopolymer Delrin 511DP is a medium viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage less s..
Tensile Strength, Yield	74.0 MPa	10700 psi	5 mm/min; ISO 527
Eurostar Starflam PX07037 PA6, Flame Retardant, Injection Molded Starflam PX07037 is an Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant, Polyamide 6 Injection Molding Resin (IR laser marking grade)Information provided by Eurostar.
Tensile Strength, Yield	73.5 MPa	10700 psi	ISO 527-1/-2
DuPont Performance Polymers Delrin® 500PE BK602 Acetal (POM)  (Unverified Data**) Medium Viscosity Acetal Homopolymer with Very Low Emissions Delrin 500PE BK602 (formerly DE20578) is a medium viscosity acetal homopolymer an enhanced version of Delrin 500P with very low VOC emissi..
Tensile Strength, Yield	74.0 MPa	10700 psi	conditioned 15 days, 23°C - 50 % R.H.; ISO 527
Arkema Group Rilsan® Clear G170 Polyamide Rilsan® Clear G170 is a high performance transparent polyamide with outstanding thermal resistance. This grade has been designed for extrusion and injection molding applications and for medical use..
Tensile Strength, Yield	74.0 MPa @Temperature 80.0 °C	10700 psi @Temperature 176 °F	ISO Data
BASF Ultramid® A3EG3 15% Glass Filled PA66 (Dry) Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500.
Tensile Strength, Yield	74.0 MPa	10700 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL32XXP PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL32XXP is a compound based on Polycarbonate resin containing Glass Fiber, PTFE.
Tensile Strength, Yield	74.0 MPa	10700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFP32 PC LNP* LUBRICOMP* DFP32 is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Tensile Strength, Yield	74.0 MPa	10700 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOTUF VX99810 Super Tough Nylon Super Tough Nylon, Proprietary Filler(s),
Tensile Strength, Yield	74.0 MPa	10700 psi	ASTM D638
Custom Resins Norpex® 2000 PPE (Polyphenylene Ether), 20% Mineral Reinforced  (discontinued **) Properties for dry as molded samples.Data provided by the manufacturer