Solvay Specialty Polymers Ixef® 3008 Polyarylamide (PARA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyarylamide (PAA)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 3008 Polyarylamide (PARA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef 3008 is a 30% carbon-fiber reinforced polyarylamide compound which exhibits extremely high strength and stiffness, good surface gloss, excellent creep resistance, and lower density than glass-fiber reinforced engineering resins. Black: Ixef 3008/9008Injection Notes: Hot Runners: 250°C to 260°C (482°F to 500°F) Injection Pressure: rapid Drying The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). Injection Molding IXEF 3008 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250°C to 260°C (482°F to 500°F) in the rear zone, gradually increasing to 260°C to 280°C (500°F to 536°F) in the front zone. If hot runners are used, they should be set to 250°C to 260°C (482°F to 500°F). To maximize crystallinity, the temperature of the mold cavity surface must be held between 120°C and 140°C (248°F and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95%-99%).Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Filler Content 30 %
30 %
Carbon Fiber Reinforcement
Water Absorption 0.22 %

@Temperature 23.0 °C,
Time 86400 sec
0.22 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.0 %
2.0 %
65% RH; Internal Method
Linear Mold Shrinkage, Flow 0.00030 - 0.0010 cm/cm
0.00030 - 0.0010 in/in
Internal Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 250 MPa
36300 psi
ISO 527-2
Elongation at Break 1.3 %
1.3 %
ISO 527-2
Tensile Modulus 26.0 GPa
3770 ksi
ISO 527-2
Flexural Strength 360 MPa
52200 psi
ISO 178
Flexural Modulus 23.0 GPa
3340 ksi
ISO 178
Izod Impact, Notched 0.590 J/cm
1.11 ft-lb/in
ASTM D256
4.50 J/cm
8.43 ft-lb/in
ASTM D256
Charpy Impact Unnotched 3.60 J/cm²
17.1 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.360 J/cm²
1.71 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
Unannealed; ISO 75-2/A
Flammability, UL94 HB
HB
UL 94
Oxygen Index 23 %
23 %
ISO 4589-2
Electrical Properties Metric English Comments
Volume Resistivity 3000 ohm-cm
3000 ohm-cm
ASTM D257
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C
248 °F
Dry Time 0.500 - 1.50 hour
0.500 - 1.50 hour
Descriptive Properties Value Comments
Appearance Black
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
High Flow
High Strength
Low Moisture Absorption
Outstanding Surface Finish
Ultra High Stiffness
Forms Pellets
Generic PARA
Processing Method Injection Molding
Uses Appliance Components
Appliances
Automotive Applications
Automotive Electronics
Automotive Under the Hood
Bushings
Camera Applications
Cams
Cell Phones
Electrical/Electronic Applications
Furniture
Gears
Industrial Applications
Lawn and Garden Equipment
Machine/Mechanical Parts
Metal Replacement
Power/Other Tools