SABIC Innovative Plastics NORYL GFN3 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GFN3 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. 30% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings, pump impellers and water meter components.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.6 g/10 min @Load 5.00 kg, Temperature 300 °C |
8.6 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 7.0 g/10 min @Load 5.00 kg, Temperature 300 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 108 | 108 | ASTM D785 |
| Tensile Strength at Break | 116 MPa | 16800 psi | Type I, 5 mm/min; ASTM D638 |
| 117 MPa | 17000 psi | ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.74 GPa | 1270 ksi | 1 mm/min; ISO 527 |
| 9.15 GPa | 1330 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 183 MPa | 26500 psi | ISO 178 |
| Flexural Yield Strength | 162 MPa | 23500 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 180 MPa | 26100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 7.17 GPa | 1040 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 8.00 GPa | 1160 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 8.71 GPa | 1260 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| 1.24 J/cm @Temperature -30.0 °C |
2.32 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 5.88 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| 35.0 kJ/m² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.90 J/cm² | 18.6 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 4.70 J/cm² @Temperature -30.0 °C |
22.4 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/2C |
| 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 61.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 158 °C @Thickness 6.40 mm |
316 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 143 °C | 289 °F | Rate B/50; ISO 306 |
| 147 °C | 297 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 90.0 °C | 194 °F | UL 746B |
| UL RTI, Mechanical with Impact | 90.0 °C | 194 °F | UL 746B |
| UL RTI, Mechanical without Impact | 90.0 °C | 194 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Oxygen Index | 26 % | 26 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.93 @Frequency 50.0 - 60.0 Hz |
2.93 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Dielectric Strength | 21.6 kV/mm @Thickness 3.20 mm |
549 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.00090 @Frequency 50.0 - 60.0 Hz |
0.00090 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 7.0 - 15 sec | 7.0 - 15 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1100V-10 Fiberglass Reinforced Thermoset BMC
- Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler
- Kingfa JH950-402 Flame Retardant PC/ABS Alloy
- Spartech Sungard Ultra Weatherable Polycarbonate Sign Grade Sheet
- Saint-Gobain Spectrosil® 2200 Optical Fused Quartz
- Wellman Wellamid® 22LH-N Unfilled Nylon 66, Lubricated & Heat Stabilized
- Total MDPE 3802 Blue Medium Density Polyethylene, Stripes
- A. Schulman POLYTROPE™ TPP 1008-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- AK Steel CARLITE® M-6 Grain Oriented Electrical Steel
- Haynes 25 alloy, room temperature after 10% cold reduction
Copyright © lookpolymers.com All Rights Reserved