- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 288 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 288 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing 10% Glass Beads and 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp DFI12E PC (Asia Pacific) LNP* Lubricomp* DFI12E is a compound based on Polycarbonate resin containing Glass Fiber, Silicone. Added features of this material include: Internally Lubricated, Easy Molding.This data was suppli.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP DL001 PC LNP* LUBRICOMP* DL001 is a compound based on Polycarbonate resin containing 5% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP DL001 PC (Asia Pacific) LNP* Lubricomp* DL001 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DL001 PC (Asia Pacific) LNP* Lubricomp* DL001 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp DFI12E PC LNP* Lubricomp* DFI12E is a compound based on Polycarbonate resin containing Glass Fiber, Silicone. Added features of this material include: Internally Lubricated, Easy Molding.This data was suppli.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
ASTM D648 |
| Kingfa JH720 G15 15% Glass Fiber Reinforced PC Features:Excellent balance propertiesHigh mechanical propertiesHigh stiffnessGood size stabilityGood surfaceApplications:Imaging equipment shellOA body frameElectrical equipmentComputer plug partsIn.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 4.00 mm |
288 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1300-22 Polycarbonate Resin Description: LUPOY PC 1300-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 4.00 mm |
288 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1621-02 Polycarbonate Resin Description: LUPOY PC 1621-02 resin is designed for large injection stretch blow molding and extrusion blow molding parts. It exhibits an excellent physical property balance of heat resistance, tran.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 4.00 mm |
288 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1302HP-22 Polycarbonate Resin Description: LUPOY PC 1302HP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS (Asia Pacific) PPE+PS blend. 20% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 listing. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRILOY D2000 PC LNP LUBRILOY* D2000 is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRILOY DF204 PC LNP* LUBRILOY* DF204 is a compound based on Polycarbonate resin containing 20% Glass Fiber, Proprietary Lubricant. Added feature of th is grade is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ISO 75 |
| Teijin Panlite® L-1250Z100 Transparent and Weather Resistant grade Polycarbonate Resin Conforms to SAE regulations. It is an injection molding grade that has normal fluidity and weather resistance and is bluish-tinted to exhibit clear color.Applications:Components of mechanical, elect.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 6.40 mm |
288 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® HN-3102G PC, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | annealed; ASTM D648 |
| Styron CALIBREâ„¢ 301 EP Polycarbonate Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Annealed; ISO 75-2/B; ASTM D648 |
| Styron CALIBREâ„¢ 302V-6 Polycarbonate Resin Overview: CALIBREâ„¢ 302V-6 Polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity (for tinted/transparent colors), and is available in both tint.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl MX5569 PPE+PS PPE+PS blend. High Heat. Good balance of flow and impact. Offers good aging performance under heat. Typical applications include Automotive Interiors and Lighting.This data was supplied by SABIC-.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 234 20% Mineral Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 234 is an injection molding grade, 20% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance, high stiffness and lo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 234 20% Mineral Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 234 is an injection molding grade, 20% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance, high stiffness and lo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | |
| Covestro Makrolon® 3108 Polycarbonate, Extrusion Grade Injection molding and extrusion grade with high viscosity, BgVV- and FDA grade for food contact applications.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ISO 75-1/-2 |
| Covestro Makrolon® 3206 Polycarbonate ISO 7391-PC,M,(,,)-05-9MVR (300 °C/1.2 kg) 4.0 cm3/10 minFood contact qualityHigh viscosityGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CExtrusionAvailable in transpar.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ISO 75-1/-2 |
| Covestro Makrolon® 9415 Polycarbonate, 10% Glass Filled ISO 7391-PC,MFR,(,,)-09-9,GF10Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 min10 % Glass fiber reinforcedChlorine- and bromine-free flame retardantUL 94V-0/1.5 mm and 5VA/3.0 mmHigh viscosityEasy rel.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ASTM D648 |
| ExxonMobil Paxon™ 7204 Crosslinkable Rotational Molding Resin Product Description: Paxon™ 7000 series of crosslinkable mHDPE resins are designed to offer outstanding ESCR, toughness, thermal, impact and notch failure resistance. These resins are ideally suite.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ASTM D648 |
| Aaron Industries AAROPRENE® GFPP 2020 Glass Filled Polypropylene AAROPRENE® GFPP 2000 Series Glass Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ISO 75 |
| Teijin Panlite® G-3410H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin Reinforced with 10 % of special GF and improved appearance grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPreci.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC (Asia Pacific) LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® LC108 PC (Asia Pacific) Polycarbonate base, 8% carbon fiber reinforced, FR |
|||