SABIC Innovative Plastics Valox® FXV310SK PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® FXV310SK PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VALOX FXV310SK is an unreinforced PBT injection moulding Visualfx* resin with high flow characteristics and containing a metal sparkle. Applications: automotive bezels and appliances.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.34 % | 0.34 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.019 - 0.024 cm/cm @Thickness 3.20 mm |
0.019 - 0.024 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 27.5 g/10 min @Load 2.16 kg, Temperature 250 °C |
27.5 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ISO 2039-2 |
| Hardness, H358/30 | 85.0 MPa | 12300 psi | ISO 2039-1 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | Type I, 50 mm/min; ASTM D638 |
| 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 15 % | 15 % | 50 mm/min; ISO 527 |
| 100 % | 100 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min; ISO 527 |
| 20 % | 20 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.70 GPa | 392 ksi | 5 mm/min; ASTM D638 |
| 2.75 GPa | 399 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.41 GPa | 350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.75 GPa | 399 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| 0.580 J/cm @Temperature -30.0 °C |
1.09 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/2C |
| 0.600 J/cm² | 2.86 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 56.0 J @Temperature 23.0 °C |
41.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 9.0 | 9.0 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 130 µm/m-°C @Temperature 0.000 - 100 °C |
72.2 µin/in-°F @Temperature 32.0 - 212 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 130 µm/m-°C @Temperature -20.0 - 150 °C |
72.2 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 55.0 °C @Thickness 3.20 mm |
131 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 185 °C | 365 °F | Rate B/50; ASTM D1525 |
| 185 °C | 365 °F | Rate B/50; ISO 306 | |
| 187 °C | 369 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 by SABIC-IP |
| HB @Thickness 3.12 mm |
HB @Thickness 0.123 in |
UL 94 by SABIC-IP | |
| Oxygen Index | 20 % | 20 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 50.0 - 60.0 Hz |
3.3 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 18.0 kV/mm @Thickness 3.20 mm |
457 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz |
0.0020 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Huntsman AVALON® 65 DE Thermoplastic Polyurethane
- Teknor Apex APEX® 3800-60 Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics NORYL PX1278 PPE+PS
- ExxonMobil Gargoyle Arctic 234 SHC 200 Series
- A. Schulman SCHULAMID® 6 GF33 33% Glass Fiber Reinforced Nylon 6
- A. Schulman SCHULAMID® 6 GF50H 50% Glass Fiber Reinforced Nylon 6
- A. Schulman POLYPUR™ FPU 1103F Thermoplastic Polyurethane Compound
- ELASTO UK Mediprene™ 660440M TPE, Medical Applications, 44A Hardness
- Epoxy Technology EPO-TEK® MA-5 Optical Grade Epoxy
- Fainplast Compounds GS 7006 Flexible PVC, Injection Molding for Footwear
Copyright © lookpolymers.com All Rights Reserved