SABIC Innovative Plastics Cycolac® G366 ABS (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Cycolac®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Cycolac® G366 ABS (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CYCOLAC G366 is a "new technology" grade of ABS exhibiting outstanding property balance, a good flow, medium impact, medium to high heat resistant and an excellent stability during injection moulding. It is recommanded for for large or complex parts in automotive, electrical power tool segments and consumer industry.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	1.0 % @Temperature 23.0 °C	1.0 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	on tensile bar; SABIC Method
Melt Flow	8.0 g/10 min @Load 10.0 kg, Temperature 220 °C	8.0 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133
	8.0 g/10 min @Load 10.0 kg, Temperature 220 °C	8.0 g/10 min @Load 22.0 lb, Temperature 428 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	115	115	ISO 2039-2
Hardness, H358/30	99.0 MPa	14400 psi	ISO 2039-1
Tensile Strength at Break	30.0 MPa	4350 psi	5 mm/min; ISO 527
	40.0 MPa	5800 psi	50 mm/min; ISO 527
Tensile Strength, Yield	45.0 MPa	6530 psi	5 mm/min; ISO 527
	50.0 MPa	7250 psi	50 mm/min; ISO 527
Elongation at Break	15 %	15 %	5 mm/min; ISO 527
	15 %	15 %	50 mm/min; ISO 527
Elongation at Yield	2.0 %	2.0 %	5 mm/min; ISO 527
	3.0 %	3.0 %	50 mm/min; ISO 527
Tensile Modulus	2.60 GPa	377 ksi	1 mm/min; ISO 527
Flexural Yield Strength	74.0 MPa	10700 psi	2 mm/min; ISO 178
Flexural Modulus	2.60 GPa	377 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	6.00 kJ/m² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
	12.0 kJ/m² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	80104; ISO 180/1A
Charpy Impact, Notched	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	V-notch Edgew 80104 sp=62mm; ISO 179/1eA
	1.20 J/cm² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80104 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles	100 @Load 1.00 kg	100 @Load 2.20 lb	CS-17; SABIC Method

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	80.0 µm/m-°C @Temperature 23.0 - 60.0 °C	44.4 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
CTE, linear, Transverse to Flow	80.0 µm/m-°C @Temperature 23.0 - 60.0 °C	44.4 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Thermal Conductivity	0.200 W/m-K	1.39 BTU-in/hr-ft²-°F	ISO 8302
Deflection Temperature at 0.46 MPa (66 psi)	96.0 °C	205 °F	Edgew 120104 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi)	82.0 °C	180 °F	Edgew 120104 sp=100mm; ISO 75/Ae
Vicat Softening Point	106 °C	223 °F	Rate B/50; ISO 306
	108 °C	226 °F	Rate B/120; ISO 306
UL RTI, Electrical	80.0 °C	176 °F	UL 746B
UL RTI, Mechanical with Impact	80.0 °C	176 °F	UL 746B
UL RTI, Mechanical without Impact	80.0 °C	176 °F	UL 746B
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	UL 94
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	2nd value; UL 94
Flame Spread	25.0 mm/min @Thickness 1.00 mm	0.984 in/min @Thickness 0.0394 in	FMVSS 302
Glow Wire Test	650 °C @Thickness 3.20 mm	1200 °F @Thickness 0.126 in	Glow Wire Flammability Index; IEC 60695-2-12
	750 °C @Thickness 1.00 mm	1380 °F @Thickness 0.0394 in	Glow Wire Flammability Index; IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	ROA; IEC 60093
Dielectric Constant	2.8 @Frequency 1.00e+6 Hz	2.8 @Frequency 1.00e+6 Hz	IEC 60250
	2.9 @Frequency 50.0 - 60.0 Hz	2.9 @Frequency 50.0 - 60.0 Hz	IEC 60250
Dielectric Strength	18.0 kV/mm @Thickness 3.20 mm	457 kV/in @Thickness 0.126 in	in oil; IEC 60243-1
	26.0 kV/mm @Thickness 1.60 mm	660 kV/in @Thickness 0.0630 in	in oil; IEC 60243-1
	35.0 kV/mm @Thickness 0.800 mm	889 kV/in @Thickness 0.0315 in	in oil; IEC 60243-1
Dissipation Factor	0.011 @Frequency 50.0 - 60.0 Hz	0.011 @Frequency 50.0 - 60.0 Hz	IEC 60250
	0.014 @Frequency 1.00e+6 Hz	0.014 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	575 V	575 V	IEC 60112

Descriptive Properties	Value	Comments
Ball Pressure Test, 75°C +/- 2°C	PASSES	IEC 60695-10-2