PolyOne Geon™ HTX L1502 Polyvinyl Chloride Alloy (PVC Alloy)
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ HTX L1502 Polyvinyl Chloride Alloy (PVC Alloy).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Physical properties based on Geon HTX L1502 white 1000.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 78 | 78 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 48.9 MPa | 7090 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.72 GPa | 395 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 2.97 GPa | 431 ksi | ASTM D790 |
| Izod Impact, Notched | 0.510 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.955 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256A |
| Dart Drop Total Energy | 57.8 J/cm @Temperature 23.0 °C |
0.108 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 57.8 J/cm @Temperature 23.0 °C |
0.108 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.0 µm/m-°C | 36.7 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 83.9 °C @Treatment Temp. 60.0 °C, Thickness 3.18 mm |
183 °F @Treatment Temp. 140 °F, Thickness 0.125 in |
Annealed; ASTM D648 |
| 88.3 °C @Treatment Temp. 50.0 °C, Thickness 3.18 mm |
191 °F @Treatment Temp. 122 °F, Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C @Treatment Temp. 50.0 °C, Thickness 3.18 mm |
181 °F @Treatment Temp. 122 °F, Thickness 0.125 in |
Annealed; ASTM D648 |
| 85.4 °C @Treatment Temp. 60.0 °C, Thickness 3.18 mm |
186 °F @Treatment Temp. 140 °F, Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 204 °C | 379 - 399 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Medium Heat Resistance | |
| Medium Impact Resistance | ||
| Forms | Cube | |
| Generic Material | PVC Alloy | |
| Generic Name | Polyvinyl Chloride Alloy (PVC Alloy) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 12445 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Building Materials | |
| Siding Substrate |
Users viewing this material also viewed the following:
- RheTech Products FT5100-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
- Nylene® 409 Nylon 6
- Mitsui AURUM® JCN6230 Thermoplastic Polyimide Resin, Amorphous (discontinued **)
- PolyOne Therma-Tech™ NJC-7500 Nylon 12 (discontinued **)
- H.C. Starck Amperit® 110.074 Agglomerated Sintered (Mo-Mo2C)
- DuPont Teijin Films Teijin® Tetoron® G2 Polyester Film, 75 Gauge
- ConocoPhillips 80W-90 Universal Gear Lubricant
- Arlon 44571B008 0.0085" (0.216 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Hippe PF GC 201 Woven Glass Cloth Reinforced Phenolic Resin - Sheet
Copyright © lookpolymers.com All Rights Reserved