RheTech Products M15P101-01 15% Mica Reinforced Polypropylene, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Mica Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products M15P101-01 15% Mica Reinforced Polypropylene, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Air ducts - distributionFan shroudsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 15 % | 15 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0114 cm/cm | 0.0114 in/in | ASTM D955 |
| Melt Flow | 23 g/10 min @Load 2.16 kg, Temperature 230 °C |
23 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | ASTM D2240 |
| Tensile Strength at Break | 30.3 MPa | 4400 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 2.34 GPa | 340 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Temperature 23.0 °C |
0.600 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.339 J | 0.250 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.9 °C | 147 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 - 221 °C | 380 - 430 °F | |
| Middle Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Front Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Nozzle Temperature | 210 - 221 °C | 410 - 430 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Lanxess Durethan® TP 140-009 901510 Nylon 6, 15% Glass Fiber
- A. Schulman POLYAXIS® PD2000 Polypropylene
- Zylog Hipolyene® 2703 MS EX 3 Thermoplastic Polyolefin & PP Compound
- ExxonMobil Exxtral™ BNU 013 Performance Polyolefin
- ConocoPhillips 2 HD Calcium Grease NLGI No. 2
- 3M Scotchcal™ 1000-98 Graphic Film
- BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned)
- Aaron Industries AVPS H 100-3 Virgin Polystyrene
Copyright © lookpolymers.com All Rights Reserved