Thermoseal KLINGERSIL® C-6327 SBR Binder Gasketing
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Styrene Butadiene Rubber |
| Manufacturer | Thermoseal Inc. |
| Trade Name | KLINGERSIL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Thermoseal KLINGERSIL® C-6327 SBR Binder Gasketing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Synthetic FiberModified SBR BinderControlled SwellUse for Low Temperatures and Low PressuresGood with Low Bolt LoadsInformation provided by Thermoseal Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM F1315 |
| Thickness | 1588 microns | 62.52 mil | Thickness tested |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 13.0 kV/mm | 330 kV/in | ASTM D149-95a |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White | (Top/Bottom) |
| Compressibility | 15 percent | ASTM F36J |
| Creep Relaxation | 35 percent | 1/32", ASTM F38B |
| Gas Permeability | <0.5 ml/min | DIN 3535/6 |
| Klinger Hot Compression Test | 16 percent | Initial, Thickness Decrease 73°F (23°C) |
| 25 percent | Additional, Thickness Decrease 572°F (300°C) | |
| Leachable Chloride Content | 150 ppm | FSA Method (Typical) |
| Recovery | >40 percent | ASTM F36J |
| Sealability | <0.2 ml/hr | 1/32", ASTM F37A |
| Thickness Increase | 0-10% | ASTM F146 after immersion in ASTM Oil 1, 5h/300°F (149°C) |
| 0-15% | ASTM Fuel A, 5h/73°F (23°C) | |
| 20-35% | ASTM Fuel B, 5h/73°F (23°C) | |
| 30-40% | ASTM Oil IRM903, 5h/300°F (149°C) | |
| Weight Increase | <35% | ASTM F146 after immersion in Fuel B 5h/73°F (23°C) |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FL910 PC
- Fiberfil® J-60/10/E/M Polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled
- Mapal Plastics Maplon CFA-HK Polypropylene Sheet
- Meilian Chemical PE650 GREEN MASTERBATCH
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A
- Dow HDPE 65053N High Density Polyethylene
- Asahi Kasei Xyron® X0718 Modified Polyphenylene Ether
- Bhansali Engineering Abstron MIF-35 ABS Injection Molding Grade
- BASF Elastollan® 1190A Polyether Type Polyurethane Elastomer
- Solvay Specialty Polymers Ixef® 2530/X9027 Polyarylamide, 55% Mineral + Glass Fiber, DAM (discontinued **)<
Copyright © lookpolymers.com All Rights Reserved