RheTech Products GC10P200-00 10% Glass Fiber Reinforced Polypropylene Copolymer, Non-UV Stabilized, Chemically Coupled, Natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Glass Fiber Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products GC10P200-00 10% Glass Fiber Reinforced Polypropylene Copolymer, Non-UV Stabilized, Chemically Coupled, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Component housingsStorage binsRecreational vehicle trim and bumpersInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 10 % | 10 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0032 cm/cm | 0.0032 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 32 | 32 | ASTM D2240 |
| Tensile Strength at Break | 37.9 MPa | 5500 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.83 GPa | 265 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 1.71 J/cm @Temperature 23.0 °C |
3.20 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 3.62 J | 2.67 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 - 221 °C | 380 - 430 °F | |
| Middle Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Front Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Nozzle Temperature | 210 - 221 °C | 410 - 430 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA (Europe-Africa-Middle East)
- A. Schulman COMTUF® 420 Impact Modified PBT
- ChevronTexaco Gear Compounds EP, ISO 680
- DuPont Teijin Films Melinex® ST504 Polyester Film, 500 Gauge
- Bapolene® 5065NB Polypropylene Impact Copolymer
- Asahi Kasei Leona® TR380 Nylon 66
- Asahi Kasei Thermofil P-20TC-0734 20% Talc Filled, High Impact, Heat Stabilized
- ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel, 34.5% Cold Work
- Gromax CFG30-QN11N1 Nylon 6 30% Glass Filled (Conditioned)
- Dow PELLETHANE® 2103-75D Film Grade Thermoplastic Polyurethane Elastomer (discontinued **)