- RheTech Products G30P100-00 30% Glass Fiber Reinforced Polypropylene, Natural
RheTech Products G30P100-00 30% Glass Fiber Reinforced Polypropylene, Natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products G30P100-00 30% Glass Fiber Reinforced Polypropylene, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Fender apronsUnderhood componentsStructural componentsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 30 % | 30 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0022 cm/cm | 0.0022 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 74 | 74 | ASTM D2240 |
| Tensile Strength at Break | 82.7 MPa | 12000 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 4.96 GPa | 720 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.565 J | 0.417 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 314 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Middle Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Front Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Nozzle Temperature | 221 - 232 °C | 430 - 450 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- MetalTek Bearium® B-4 Bearing Bronze
- Lubrizol Advanced Materials Pearlthane® MB-9005 Thermoplastic Polyurethane Elastomer
- Techmer ES Electrablend® PA12 CF13 L 13% Carbon Filled
- SMAC SMACMOUNT® 2527S Damping Material
- A. Schulman FORMION™ FI 231 5% Mineral Reinforced Ionomer / Nylon Alloy
- Eastman Tenite Butyrate 580A3720016 Clear, Trsp Cellulose Acetate Butyrate
- C.O.I.M. EXTER S® S 401 Isophthalic Resin
- Alliance Polymers Viprene™ P85A-22U-BLK Thermoplastic Vulcanizate Elastomer
- A. Schulman POLYPUR™ CB 1110 Thermoplastic Polyurethane Compound
- Lehmann & Voss LUVOCOM® 1105-8135/OR PEEK, unreinforced, easy flowing
Copyright © lookpolymers.com All Rights Reserved