SABIC Innovative Plastics NORYL EXNL1117 PPE+HIPS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL EXNL1117 PPE+HIPS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
high gloss Noryl
Physical Properties Metric English Comments
Specific Gravity 1.12 g/cc
1.12 g/cc
ASTM D792
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Water Absorption at Saturation 0.060 %
0.060 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 280 °C
25 g/10 min

@Load 4.76 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 25 g/10 min

@Load 2.16 kg,
Temperature 280 °C
25 g/10 min

@Load 4.76 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min; ISO 527
67.0 MPa
9720 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 4.4 %
4.4 %
50 mm/min; ISO 527
5.2 %
5.2 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 3.3 %
3.3 %
50 mm/min; ISO 527
3.6 %
3.6 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.56 GPa
371 ksi
5 mm/min; ASTM D638
2.81 GPa
408 ksi
1 mm/min; ISO 527
Flexural Yield Strength 100 MPa
14500 psi
1.3 mm/min, 50 mm span; ASTM D790
100 MPa
14500 psi
2 mm/min; ISO 178
Flexural Modulus 2.65 GPa
384 ksi
2 mm/min; ISO 178
2.73 GPa
396 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
0.200 J/cm

@Temperature -30.0 °C
0.375 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 30.0 J

@Temperature 23.0 °C
22.1 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 77.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
77.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 79.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
79.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
75.0 °C

@Thickness 3.20 mm
167 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 96.0 °C
205 °F
Rate B/50; ASTM D1525
96.0 °C
205 °F
Rate B/50; ISO 306
98.0 °C
208 °F
Rate B/120; ISO 306
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
UL 94 by SABIC-IP
V-0

@Thickness 2.50 mm
V-0

@Thickness 0.0984 in
UL 94 by SABIC-IP